quakercoat547

TECHNICAL DATA SHEET QUAKERCOAT® 547

TUBE AND PIPE PROTECTIVE COATING

QUAKERCOAT® 547 is a solvent-based, high solids coating intended for use as a decorative corrosion inhibiting coating on metal, particularly tube and pipe surfaces.

Benefits

Applications

igh solids technology results in greater coating • Hcoverage per gallon of product, thus reducing

Use standard air spray or airless spray equipment.

Clean equipment with appropriate solvent while residue is still wet.

ostly surface corrosion is inhibited because of • Cinherent consistent film uniformity

Compatibility Quaker Houghton also provides the full range of fluids for the manufacture of tube & pipe. This includes coolants for forming and sawing, cleaning compounds and corrosion preventives for in-process and final corrosion protection.

Consult your Quaker Houghton representative.

Health, Safety and Handling

applied coating costs

lean-up costs are minimized due to drying • Cproperties and minimal drain-off and drippage elatively low VOC content allows use in many • Rlocations where VOC limitations are stringent

Properties - Coating PROPERTIES

TYPICAL VALUE

Please consult the Safety Data Sheet (SDS) for information on storage, safe handling and disposal. The conditions or methods of handling, storage, use and disposal of the product are beyond our reasonable control - we assume no liability for any ineffectiveness of the product or any injury or damage, arising out of or in connection with these conditions.

Appearance

Amber Liquid

Properties - Cured Film CURED FILM Dry Time (Tack Free) *

40 - 50 mins

Abrasion Resistance

Very Good

Corrosion Resistance Salt Fog (ASTM B117)

Excellent

Chemical Resistance

Very Good

Recommended Dry Film Thickness

1.0 - 1.4 mils

Recommended Wet Film Thickness

2.2 - 3.0 mils

Pounds per gallon at 60ºF

7.68

lbs/gal

42 | >107

°C | °F

15 - 25

secs

VOC (Excluding Water and Exempts)

3.5 420

lbs/gal gms/liter

Coverage at 1.0mil Dry Film

738

ft2/gal

Volume Solids

46%

Weight Solids

54%

Flash Point via TCC Viscosity at 77 F (#3 Zahn Cup) o

* Affected by air temperature, humidity, volume or air movement across drying surface.

©2019 Quaker Houghton. All rights reserved.

UNIT

quakerhoughton.com | info@quakerhoughton.com

QUAKERCOATÂŽ 547

TUBE AND PIPE PROTECTIVE COATING

Fluid Maintenance The following directions and recommendationsare intended to serve as a guide and may require modification to meet local conditions.

Mixing: Mix as necessary to avoid separation.

Thinning: Use as received. If conditions warrant thinning, use an appropriate solvent that is in compliance with local environmental regulations and specific requirements.

Please note that the further addition of solvent will affect the VOC content of the product. The VOC content listed is solely for the product as received.

Surface Preparation: The intended substrate must be clean and dry to accept the protective coating properly. Loose debris, dust, oil, or other contamination may degrade product effectiveness and performance.

Cure Cycle: Air cure time will vary depending on the temperature, humidity, substrate temperature and wet film thickness. Dry time may be substantially reduced by increasing air flow and temperature across sprayed items or pre-heating the parts to be painted.

All reasonable care has been taken to ensure this publication is accurate upon issue. Such information may be affected by changes subsequent to issue. This Technical Data Sheet is to be used solely for this product. Prior to any use, consult the Safety Data Sheet (SDS) for information on hazard risks and product use parameters. All liability and all warranties express or implied are hereby excluded as to product performance results, the accuracy of these data including any warranty of merchantability or fitness for any purpose. 014512