QUOTE No.: NC8635
Certificate of Test
REPORT No.: FNC12918
COMBUSTIBILITY TEST FOR MATERIALS IN ACCORDANCE WITH AS 1530.1-1994
TRADENAME: Haymes Rendertex Renderbase Q High Polymer Strength (HPS)
SPONSOR: Henry Haymes Proprietary Limited Trading as Haymes Paints 1 Waringa Drive
Wendouree Industrial Park
BALLARAT VIC 3355
AUSTRALIA
DESCRIPTION OF
TEST SAMPLE: The sponsor described the tested specimen as a polymer rich cement based render comprised of sand, crystalline silica, cement, calcium hydroxide and non-hazardous ingredients.
Nominal thickness: 50 mm
Nominal density: 1399.49 kg/m³ Colour: off-white
TEST PROCEDURE: Five (5) samples were tested in accordance with Australian Standard 1530 Methods for fire tests on building materials, components and structures, Part 1- 1994: Combustibility Test for Materials.
An alternative suitable insulating material was used to fill the annular space between the furnace tubes, as specified in Clause 4.2 of ISO 1182:2010.
RESULTS: The following calculated results were obtained, refer also to Summary of measurements:
DESIGNATION: The material is deemed COMBUSTIBLE according to the test criteria specified in Clause 3.4 of AS 1530.1-1994.
These test results relate only to the behaviour of the test specimens of the material under the particular conditions of the test and they are not intended to be the sole criterion for assessing the potential fire hazard of the material in use.
DATE OF TEST: 10 May 2022
Issued on the 8th day of June 2022 without alterations or additions.
Faustin Molina
Stephen Smith
Testing Officer Team Leader, Reaction to Fire & Façade Fire Laboratory
End of Report
Copyright CSIRO 2022 ©. Copying or alteration of this report without written authorisation from CSIRO is forbidden NATA Accredited Laboratory Number: 165
Corporate Site No 3625
Accredited for compliance with ISO/IEC 17025 - Testing
Page 1 of 2
Arithmetic mean = ���������������� �� Mean furnace thermocouple temperature rise (oC) 0.57 Mean specimen centre thermocouple temperature rise (oC) 0.12 Mean specimen surface thermocouple temperature rise (oC) 0.72 Mean duration of sustained flaming (s) 143.6 Mean mass loss (%) 9.04
End of Test Certificate
Page 2 of 2
OF MEASUREMENTS AND OBSERVATIONS OF SAMPLES UNDER TEST C12918 Parameters Symbol or expression Unit symbol Sample Number 1 2 3 4 5 Initial specimen mass msi g 112.74 109.37 111.78 108.56 109.51 Final specimen mass msf g 102.87 99.87 101.60 98.17 99.55 Mass loss �� = Msi ������ ������ x 100 % 8.75 8.69 9.11 9.57 9.10 Total duration of sustained flaming Cumulative total of duration of flaming* s 70 173 171 92 212 Initial furnace thermocouple temperature Tfi oC 749 752 749 748 754 Maximum furnace thermocouple temperature Tfm oC 777 779 778 777 780 Final furnace thermocouple temperature Tff oC 776 778 778 776 780 Furnace thermocouple temperature rise ���� =������ ������ oC 1 1 1 1 0 Maximum specimen centre thermocouple temperature Tcm oC 700 697 701 692 685 Final specimen centre thermocouple temperature Tcf oC 700 696 701 692 684 Specimen centre thermocouple temperature rise ���� =������ ������ oC 0 0 0 0 0 Maximum specimen surface thermocouple temperature Tcm oC 777 777 776 775 774 Final specimen surface thermocouple temperature Tsf oC 776 777 775 773 774 Specimen surface thermocouple temperature rise ���� =������ ������ oC 1 0 1 1 0 Test duration - min 55 50 60 50 50 Any individual duration flaming less than 5 seconds was discarded
SUMMARY