Understanding nrt reading 1 2 of 2 radiogaphic testing a

Understandings NRT – Reading 1 Part 2/2 Radiographic Testing 2nd Pre-exam self study note for Neutron Radiographic Testing 7th April 2016

Charlie Chong/ Fion Zhang

NDT for Upstream

Charlie Chong/ Fion Zhang

NDT for Upstream

Charlie Chong/ Fion Zhang

NDT for Upstream

Charlie Chong/ Fion Zhang

NDT for Upstream

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

Fion Zhang at Xitang 1st April 2016

Charlie Chong/ Fion Zhang

SME- Subject Matter Expert

我们的大学,其实应该聘请这些能干的退休教授. 或许在职的砖头怕被排斥. http://cn.bing.com/videos/search?q=Walter+Lewin&FORM=HDRSC3 https://www.youtube.com/channel/UCiEHVhv0SBMpP75JbzJShqw

Charlie Chong/ Fion Zhang

BOK NR- Neutron Radiographic Testing Length: 4 hours Questions: 135

1. Principles/ Theory • Nature of penetrating radiation • Interaction between penetrating radiation and matter • Neutron radiography imaging • Radiometry

2. Equipment/Materials • Sources of neutrons • Radiation detectors • Nonimaging devices

Charlie Chong/ Fion Zhang

3. Techniques/Calibrations • Blocking and filtering • Multifilm technique • Enlargement and projection • Stereoradiography • Triangulation methods • Autoradiography • Flash Radiography • In-motion radiography • Fluoroscopy • Electron emission radiography • Microradiography • Laminography (tomography) • Control of diffraction effects • Panoramic exposures • Gaging • Real time imaging • Image analysis techniques

Charlie Chong/ Fion Zhang

4. Interpretation/Evaluation • Image-object relationships • Material considerations • Codes, standards, and specifications

5. Procedures • Imaging considerations • Film processing • Viewing of radiographs • Judging radiographic quality

6. Safety and Health • Exposure hazards • Methods of controlling radiation exposure • Operation and emergency procedures

Charlie Chong/ Fion Zhang

http://www.yumpu.com/zh/browse/user/charliechong http://issuu.com/charlieccchong

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

http://greekhouseoffonts.com/

The Magical Book of Tank Inspection ICP

Charlie Chong/ Fion Zhang

数字签名 者：Fion Zhang DN：cn=Fion Zhang, o, ou, email=fion_zhan g@qq.com, c=CN 日期：2016.04.08 10:28:05 +08'00'

Charlie Chong/ Fion Zhang

闭门练功

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

Industrial Radiography

Charlie Chong/ Fion Zhang

http://gafoorxspeed.com/industrial-radiography.html

Chapter 6: Radio Isotope (Gamma) Sources Emitted gamma radiation is one of the three types of natural radioactivity. It is the most energetic form of electromagnetic radiation, with a very short wavelength of less than one-tenth of a nano-meter. Gamma rays are essentially very energetic x-rays emitted by excited nuclei. They often accompany alpha or beta particles, because a nucleus emitting those particles may be left in an excited (higher-energy) state.

In medicine gamma-ray sources are used to treat cancer, for diagnostic purposes, and to sterilize equipment and supplies. In industry they are used in the inspection of castings and welds and in food processing to kill microorganisms and retard spoilage.

Charlie Chong/ Fion Zhang

Man made sources are produced by introducing an extra neutron to atoms of the source material. As the material rids itself of the neutron, energy is released in the form of gamma rays.

Two of the more common industrial Gamma-ray sources are iridium-192 and cobalt-60. These isotopes emit radiation in two or three discreet wavelengths. â– Cobalt-60 will emit a 1.33 and a 1.17 MeV gamma ray, and â– iridium-192 will emit 0.31, 0.47, and 0.60 MeV gamma rays.

Physical size of isotope materials will very from manufacturer, but generally an isotope is a pellet 1.5 mm x 1.5 mm. Depending on the activity (curies) desired a pellet or pellets are loaded into a stainless steel capsule and sealed by welding. New sources of cobalt will have an activity of 20 curies, and new sources of iridium will have an activity of 100 curies.

Charlie Chong/ Fion Zhang

Cobalt-60

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

https://en.wikipedia.org/wiki/Cobalt-60

Cobalt-60, 60Co, is a synthetic radioactive isotope of cobalt with a half-life of 5.2714 years. It is produced artificially in nuclear reactors. Deliberate industrial production depends on neutron activation of bulk samples of the monoisotopic and mononuclidic cobalt isotope 59Co. Measurable quantities are also produced as a by-product of typical nuclear power plant operation and may be detected externally when leaks occur. In the latter case (in the absence of added cobalt) the incidentally produced 60Co is largely the result of multiple stages of neutron activation of iron isotopes in the reactor's steel structures via the creation of 59Co precursor.

The simplest case of the latter would result from the activation of 5826Fe. 60 Co decays by beta decay to the stable isotope nickel-60 (60 Ni). The 27 28 activated nickel nucleus emits two gamma rays with energies of 1.17 and 1.33 MeV, hence the overall nuclear equation of the reaction is 59

27Co

+ n → 6027Co → 6028Ni + e− + ṽe + ɣ rays.

Charlie Chong/ Fion Zhang

Activity of Co-60 Corresponding to its half-life the radioactive activity of one gram of 60Co is 44 TBq (about 1100 curies). The absorbed dose constant is related to the decay energy and time. For 60Co it is equal to 0.35 mSv/(GBq h) at one meter from the source. This allows calculation of the equivalent dose, which depends on distance and activity.

Example: a 60Co source with an activity of 2.8 GBq, which is equivalent to 60 µg of pure 60Co, generates a dose of 1 mSv at one meter distance within one hour. The swallowing of 60Co reduces the distance to a few millimeters, and the same dose is achieved within seconds.

Test sources, such as those used for school experiments, have an activity of <100 kBq. Devices for nondestructive material testing use sources with activities of 1 TBq and more.

The high γ-energies result in a significant mass difference between 60Ni and 60Co of 0.003 μ (μg?). This amounts to nearly 20 watts (?) per gram, nearly 30 times larger than that of 238Pu. Charlie Chong/ Fion Zhang

https://en.wikipedia.org/wiki/Cobalt-60

Decay of Co-60 The decay scheme of 60Co and 60mCo. The diagram shows a (simplified) decay scheme of 60Co and 60mCo. The main β-decay transitions are shown. The probability for population of the middle energy level of 2.1 MeV by β-decay is 0.0022%, with a maximum energy of 665.26 keV. Energy transfers between the three levels generate six different gamma-ray frequencies.

In the diagram the two important ones are marked. Internal conversion energies are well below the main energy levels.

60mCo

is a nuclear isomer of 60Co with a half-life of 10.467 minutes. It decays by internal transition to 60Co, emitting 58.6 keV gamma rays, or with a low probability (0.22%) by β-decay into 60Ni.

Charlie Chong/ Fion Zhang

In the diagram the two important ones are marked. Internal conversion energies are well below the main energy levels.

Charlie Chong/ Fion Zhang

Îł-Ray Spectrum of Cobalt-60

Charlie Chong/ Fion Zhang

A nuclear isomer is a metastable state of an atomic nucleus caused by the excitation of one or more of its nucleons (protons or neutrons).

"Metastable" refers to the fact that these excited states have half-lives more than 100 to 1000 times the half-lives of the excited nuclear states that decay with a "prompt" half life (ordinarily on the order of 10−12 seconds). As a result, the term "metastable" is usually restricted to refer to isomers with half-lives of 10−9 seconds or longer. Some sources recommend 5 × 10−9 s to distinguish the metastable half life from the normal "prompt" gamma emission half life

Charlie Chong/ Fion Zhang

https://en.wikipedia.org/wiki/Nuclear_isomer

Isomers Nuclei can have the same neutron-proton composition but not be identical; one nucleus can contain more energy than the other. Two nuclei that have the same composition but varying energy are known as isomers. An example of a pair of isomers is shown below. Technetium-99 can exist in two energy states; the higher of the two is a temporary state generally referred to as a metastable state. The symbol for a nuclide in the metastable state is obtained by adding the letter m to the mass number (Tc-99m). A nucleus in the metastable state will eventually give off its excess energy and change to the other isomer. Such isomeric transitions have an important role in nuclear medicine and are discussed in detail later.

Charlie Chong/ Fion Zhang

http://www.sprawls.org/ppmi2/MATTER/

Charlie Chong/ Fion Zhang

http://www.sprawls.org/ppmi2/MATTER/

Charlie Chong/ Fion Zhang

Half-lives (example: Gd)

Charlie Chong/ Fion Zhang

Isotope half-lives. Note that the darker more stable isotope region departs from the line of protons (Z) = neutrons (N), as the element number Z becomes larger

Advantages of gamma ray sources include portability and the ability to penetrate thick materials in a relativity short time. As can be noted above cobalt will produce energies comparable to a 1.25 MeV x-ray system. Iridium will produce energies comparable to a 460 kV x-ray system. Not requiring electrical sources the gamma radiography is well adapted for use in remote locations. â&#x2013; Co-60 comparable to a 1.25 MeV x-ray system â&#x2013; Ir-192 comparable to a 0.46 MeV x-ray system Disadvantages include shielding requirements and safety considerations.

Depleted uranium is used as a shielding material for sources. The storage container (camera) for iridium sources will contain 45 pounds of shielding materials. Cobalt will require 500 pounds of shielding. Cobalt cameras are often fixed to a trailer and transported to and from inspection sites. Iridium is used whenever possible, and not all companies using source material will have a cobalt source. Source materials are constantly generating very penetrating radiation and in a short time considerable damage can be done to living tissue. Technicians must be trained in potential hazards to themselves and the public associated with use of gamma radiography.

Charlie Chong/ Fion Zhang

Because of safety issues source materials are regulated by Federal or State jurisdictions. The Nuclear Regulation Commission (NRC) has developed and enforces regulations for source material. The commission allows states to regulate materials if they follow guidelines of the commission. These states are identified as "Agreement States". In either case, obtaining and maintaining a license is a costly and well regulated process that protects workers and the public from the hazards of gamma radiation.

Typically gamma radiography is used for inspection of castings and weldments. However, other techniques and applications are being developed.

Profile radiography is one example. Profile radiography is used for corrosion under insulation. Exposures are made of a small section of the pipe wall. A cooperator block such as a Ricki T is used to calculate the blowout factor for the exposure in order to calculate the remaining wall thickness of the pipe.

The exposure source is usually iridium-192, with cobalt-60 used for the pipes of heavier wall.

Charlie Chong/ Fion Zhang

Radio Isotope - Th232 Half life: 1.405E10 Years

Radio Isotope - Ir192 Half life: 73.830 Days

Charlie Chong/ Fion Zhang

Radio Isotope - Tm170 Half life: 128.6 Days Radio Isotope - Yb169 Half life: 32.026 Days

Radio Isotope - Cs137 Half life: 30.07 Years

Charlie Chong/ Fion Zhang

Radio Isotope - Co60 Half life: 1925.1 Days

Charlie Chong/ Fion Zhang

Chapter 7: Radiographic Film X-ray films for general radiography consist of an emulsion-gelatin containing a radiation sensitive silver halide and a flexible, transparent, blue-tinted base.

The emulsion is different from those used in other types of photography films to account for the distinct characteristics of gamma rays and x-rays, but X-ray films are sensitive to light.

Usually, the emulsion is coated on both sides of the base in layers about 0.0005 inch thick (0.0127mm, 12.7Îźm) . Putting emulsion on both sides of the base doubles the amount of radiation-sensitive silver halide, and thus increases the film speed. The emulsion layers are thin enough so developing, fixing, and drying can be accomplished in a reasonable time.

A few of the films used for radiography only have emulsion on one side which produces the greatest detail in the image.

Charlie Chong/ Fion Zhang

12.7Îźm sensitive silver halide blue-tinted base

When x-rays, gamma rays, or light strike the grains of the sensitive silver halide in the emulsion, a change takes place in the physical structure of the grains. This change is of such a nature that it cannot be detected by ordinary physical methods (latent image) . However, when the exposed film is treated with a chemical solution (developer), a reaction takes place, causing formation of black, metallic silver. It is this silver, suspended in the gelatin on both sides of the base, that creates an image

Charlie Chong/ Fion Zhang

Film Selection The selection of a film when radiographing any particular component depends on a number of different factors. Listed below are some of the factors that must be considered when selected a film and developing a radiographic technique.

1. the composition, shape, and size of the part being examined and, in some cases, its weight and location.

2. the type of radiation used, whether x-rays from an x-ray generator or gamma rays from a radioactive source.

3. the kilovoltages available with the x-ray equipment or the intensity of the gamma radiation.

4. the relative importance of high radiographic detail or quick and economical results.

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

Selecting the proper film and developing the optimal radiographic technique usually involves arriving at a balance between a number of opposing factors.

For example, if high resolution and contrast sensitivity is of overall importance, a slower and hence finer grained film should be used in place of a faster film.

Charlie Chong/ Fion Zhang

Arithmetic of Exposure RELATIONS OF MILLIAMPERAGE (SOURCE STRENGTH), DISTANCE, AND TIME With a given kilovoltage of x-radiation or with the gamma radiation from a particular isotope, the three factors governing the exposure are the milliamperage (for x-rays) or source strength (for gamma rays), time, and source-film distance. The numerical relations among these three quantities are demonstrated below, using x-rays as an example. The same relations apply for gamma rays, provided the number of curies in the source is substituted wherever milliamperage appears in an equation.

The necessary calculations for any changes in focus-film distance (D), milliamperage (M), or time (T) are matters of simple arithmetic and are illustrated in the following example. As noted earlier, kilovoltage changes cannot be calculated directly but must be obtained from the exposure chart of the equipment or the operator's logbook.

All of the equations shown on these pages can be solved easily for any of the variables (mA, T, D), using one basic rule of mathematics: If one factor is moved across the equals sign (=), it moves from the numerator to the denominator or vice versa.

Charlie Chong/ Fion Zhang

We can now solve for any unknown by: 1. Eliminating any factor that remains constant (has the same value and is in the same location on both sides of the equation).

2. Simplifying the equation by moving the unknown value so that it is alone on one side of the equation in the numerator.

3. Substituting the known values and solving the equation.

Charlie Chong/ Fion Zhang

Milliamperage-Distance Relation The milliamperage employed in any exposure technique should be in conformity with the manufacturer's rating of the x-ray tube. In most laboratories, however, a constant value of milliamperage is usually adopted for convenience.

Rule: The milliamperage (M) required for a given exposure is directly proportional to the square of the focus-film distance (D). The equation is expressed as follows:

Charlie Chong/ Fion Zhang

Example: Suppose that with a given exposure time and kilovoltage, a properly exposed radiograph is obtained with 5mA (M1) at a distance of 12 inches (D1), and that it is desired to increase the sharpness of detail in the image by increasing the focus-film distance to 24 inches (D2). The correct milliamperage (M2) to obtain the desired radiographic density at the increased distance (D2) may be computed from the proportion:

Charlie Chong/ Fion Zhang

When very low kilovoltages, say 20 kV or less, are used, the x-ray intensity decreases with distance more rapidly than calculations based on the inverse square law would indicate because of absorption of the x-rays by the air. Most industrial radiography, however, is done with radiation so penetrating that the air absorption need not be considered. These comments also apply to the time-distance relations discussed below.

Charlie Chong/ Fion Zhang

Time-Distance Relation Rule: The exposure time (T) required for a given exposure is directly proportional to the square of the focus-film distance (D). Thus:

To solve for either a new Time (T2) Or a new Distance (D2), simply follow the steps shown in the example above.

Charlie Chong/ Fion Zhang

Tabular Solution of Milliamperage-Time and Distance Problems Problems of the types discussed above may also be solved by the use of a table similar to the one below. The factor between the new and the old exposure time, milliamperage, or milliamperage-minute (mA-min) value appears in the box at the intersection of the column for the new source-film distance and the row for the old source-film distance.

Suppose, for example, a properly exposed radiograph has an exposure of 20 mA-min with a source-film distance of 30 inches and you want to increase the source-film distance to 45 inches in order to decrease the geometric unsharpness in the radiograph. The factor appearing in the box at the intersection of the column for 45 inches (new source-film distance) and the row for 30 inches (old source-film distance) is 2.3. Multiply the old milliampere-minute value (20) by 2.3 to give the new value--46 mA-min.

Charlie Chong/ Fion Zhang

Note that some approximation is involved in the use of such a table, since the values in the boxes are rounded off to two significant figures. However, the errors involved are always less than 5 percent and, in general, are insignificant in actual practice.

Further, a table like the one below obviously cannot include all source-film distances, because of limitations of space. However, in any one radiographic department, only a few source-film distances are used in the great bulk of the work, and a table of reasonable size can be constructed involving only these few distances.

Charlie Chong/ Fion Zhang

Milliamperage-Time and Distance Relations

Charlie Chong/ Fion Zhang

Milliamperage-Time Relation Rule: The milliamperage (M) required for a given exposure is inversely proportional to the time (T):

Another way of expressing this is to say that for a given set of conditions (voltage, distance, etc), the product of milliamperage and time is constant for the same photographic effect.

Thus, M1T1 = M2T2 = M3T3 = C, a constant.

This is commonly referred to as the reciprocity law. (Important exceptions are discussed below.)

To solve for either a new time (T2) or a new milliamperage (M2), simply follow the steps shown in the example in "Milliamperage-Distance Relation".

Charlie Chong/ Fion Zhang

THE RECIPROCITY LAW In the sections immediately preceding, it has been assumed that exact compensation for a decrease in the time of exposure can be made by increasing the milliamperage according to the relation M1T1 = M2T2. This may be written MT = C and is an example of the general photochemical law that the same effect is produced for IT = constant, where I is intensity of the radiation and T is the time of exposure. It is called the reciprocity law and is true for direct x-ray and lead screen exposures. For exposures to light, it is not quite accurate and, since some radiographic exposures are made with the light from fluorescent intensifying screens, the law cannot be strictly applied.

Errors as the result of assuming the validity of the reciprocity law are usually so small that they are not noticeable in examples of the types given in the preceding sections. Departures may be apparent, however, if the intensity is changed by a factor of 4 or more. Since intensity may be changed by changing the source-film distance, failure of the reciprocity law may appear to be a violation of the inverse square law.

Charlie Chong/ Fion Zhang

Applications of the reciprocity law over a wide intensity range sometimes arise, and the relation between results and calculations may be misleading unless the possibility of failure of the reciprocity law is kept in mind. Failure of the reciprocity law means that the efficiency of a light-sensitive emulsion in utilizing the light energy depends on the light intensity. Under the usual conditions of industrial radiography, the number of milliampere-minutes required for a properly exposed radiograph made with fluorescent intensifying screens increases as the x-ray intensity decreases, because of reciprocity failure.

If the milliamperage remains constant and the x-ray intensity is varied by changing the focus-film distance, the compensating changes shown in the table below should be made in the exposure time.

Charlie Chong/ Fion Zhang

Approximate Corrections for Reciprocity Law Failure

1Column

2 shows the changes necessitated by the inverse square law only.

Column 3 shows the combined effects of the inverse square law and failure of the reciprocity law.

Charlie Chong/ Fion Zhang

The table gives a rough estimate of the deviations from the rules given in the foregoing section that are necessitated by failure of the reciprocity law for exposures with fluorescent intensifying screens. It must be emphasized that the figures in column 3 are only approximate. The exact values of the factors vary widely with the intensity of the fluorescent light and with the density of the radiograph.

When distance is held constant, the milliamperage may be increased or decreased by a factor of 2, and the new exposure time may be calculated by the method shown in "Time-Distance Relation", without introducing errors caused by failure of the reciprocity law, which are serious in practice.

Charlie Chong/ Fion Zhang

http://webstag.kodak.cz/US/en/business/aim/industrial/ndt/literature/radiography/07.shtml#ccurves

Film Packaging Radiographic film can be purchased in a number of different packaging options. The most basic form is as individual sheets in a box. In preparation for use, each sheet must be loaded into a cassette or film holder in the darkroom to protect it from exposure to light. The sheet are available in a variety of sizes and can be purchased with or without interleaving paper.

Interleaved packages have a layer of paper that separates each piece of film.

The interleaving paper is removed before the film is loaded into the film holder. Many users find the interleaving paper useful in separating the sheets of film and offer some protection against scratches and dirt during handling.

Industrial x-ray films are also available in a form in which each sheet is enclosed in a light-tight envelope. The film can be exposed from either side without removing it from the protective packaging. A rip strip makes it easy to remove the film in the darkroom for processing. This form of packaging has the advantage of eliminating the process of loading the film holders in the darkroom. The film is completely protected from finger marks and dirt until the time the film is removed from the envelope for processing.

Charlie Chong/ Fion Zhang

Packaged film is also available in rolls, which allows the radiographer to cut the film to any length. The ends of the packaging are sealed with electrical tape in the darkroom. In applications such as the radiography of circumferential welds and the examination of long joints on an aircraft fuselage, long lengths of film offer great economic advantage. The film is wrapped around the outside of a structure and the radiation source is positioned on axis inside allowing for examination of a large area with a single exposure.

Envelope packaged film can be purchased with the film sandwiched between two lead oxide screens. The screens function to reduce scatter radiation at energy levels below 150kV and as intensification screens above 150 kV.

Charlie Chong/ Fion Zhang

Film Handling X-ray film should always be handled carefully to avoid physical strains, such as pressure, creasing, buckling, friction, etc. Whenever films are loaded in semiflexible holders and external clamping devices are used, care should be taken to be sure pressure is uniform. If a film holder bears against a few high spots, such as on an un-ground weld, the pressure may be great enough to produce desensitized areas in the radiograph. This precaution is particularly important when using envelope-packed films.

Marks resulting from contact with fingers that are moist or contaminated with processing chemicals, as well as crimp marks, are avoided if large films are always grasped by the edges and allowed to hang free. A supply of clean towels should be kept close at hand as an incentive to dry the hands often and well. Use of envelope-packed films avoids many of these problems until the envelope is opened for processing.

Another important precaution is to avoid drawing film rapidly from cartons, exposure holders, or cassettes. Such care will help to eliminate circular or treelike black markings in the radiograph that sometimes result due to static electric discharges.

Charlie Chong/ Fion Zhang

Chapter 8: Image Considerations The most common detector used in industrial radiography is film. The high sensitivity to ionizing radiation provides excellent detail and sensitivity to density changes when producing images of industrial materials. Image quality is determined by a combination of variables: radiographic contrast and definition. Many variables affecting radiographic contrast and definition are summarized below and addressed in following sections.

Radiographic Contrast Radiographic contrast describes the differences in photographic density in a radiograph. The contrast between different parts of the image is what forms the image and the greater the contrast, the more visible features become.

Radiographic contrast has two main contributors: subject contrast and detector or film contrast.

Charlie Chong/ Fion Zhang

Subject contrast is determined by the following variables: - Absorption differences in the specimen - Wavelength of the primary radiation -Scatter or secondary radiation Film contrast is determined by the following: - Grain size or type of film - Chemistry of film processing chemicals - Concentrations of film processing chemicals - Time of development - Temperature of development - Degree of mechanical agitation (physical motion)

Charlie Chong/ Fion Zhang

Exposing the film to produce higher film densities will generally increase contrast. In other words, darker areas will increase in density faster than lighter areas because in any given period of time more x-rays are reaching the darker areas. Lead screens in the thickness range of 0.004 to 0.015 inch typically reduce scatter radiation at energy levels below 150, 000 volts. Above this point they will emit electrons to provide more exposure of the film to ionizing radiation thus increasing the density of the radiograph. Fluorescent screens produce visible light when exposed to radiation and this light further exposes the film.

Charlie Chong/ Fion Zhang

Definition Radiographic definition is the abruptness of change in going from one density to another. There are a number of geometric factors of the X-ray equipment and the radiographic setup that have an effect on definition. These geometric factors include: 1. Focal spot size, which is the area of origin of the radiation. The focal spot size should be as close to a point source as possible to produce the most definition.

2. Source to film distance, which is the distance from the source to the part. Definition increases as the source to film distance increase.

3. Specimen to detector (film) distance, which is the distance between the specimen and the detector. For optimal definition, the specimen and detector should be as close together as possible. .

4. Abrupt changes in specimen thickness may cause distortion on the radiograph.

5. Movement of the specimen during the exposure will produce distortion on the radiograph.

6. Film graininess, and screen mottling will decrease definition. The grain size of the film will affect the definition of the radiograph. Wavelength of the radiation will influence apparent graininess. As the wavelength shortens and penetration increases, the apparent graininess of the film will increase. Also, increased development of the film will increase the apparent graininess of the radiograph.

Charlie Chong/ Fion Zhang

Chapter 9: Film Processing Processing film is a strict science governed by rigid rules of chemical concentration, temperature, time, and physical movement. Whether processing is done by hand or automatically by machine, excellent radiographs require the highest possible degree of consistency and quality control.

Manual Processing & Darkrooms Manual processing begins with the darkroom. The darkroom should be located in a central location, adjacent to the reading room and a reasonable distance from the exposure area. For portability darkrooms are often mounted on pickups or trailers.

Charlie Chong/ Fion Zhang

Film should be located in a light, tight compartment, which is most often a metal bin that is used to store and protect the film. An area next to the film bin that is dry and free of dust and dirt should be used to load and unload the film.

While another area, the wet side, will be used to process the film. Thus protecting the film from any water or chemicals that may be located on the surface of the wet side.

Each of step in film processing must be excited properly to develop the image, wash out residual processing chemicals, and to provide adequate shelf life of the radiograph. The objective of processing is two fold. First to produce a radiograph adequate for viewing, and secondly to prepare the radiograph for archival storage. A radiograph may be retrieved after 5 or even 20 years in storage.

Charlie Chong/ Fion Zhang

Automatic Processor Evaluation The automatic processor is the essential piece of equipment in every x-ray department. The automatic processor will reduce film processing time when compared to manual development by a factor of four. To monitor the performance of a processor, apart from optimum temperature and mechanical checks, chemical and sensitometric checks should be performed for developer and fixer. Chemical checks involve measurement of pH values for developer and replenisher, fixer and replenisher, measurement of specific gravity and fixer silver levels. Ideally pH should be measured daily and it is important to record these measurements, as regular logging provides very useful information. The daily measurements of pH values for developer and fixer can then be plotted to observe the trend of variations in these values compared to normal pH operating levels to identify problems.

Charlie Chong/ Fion Zhang

Sensitometric checks may be carried out to evaluate if the performance of films in the automatic processors is being maximized. These checks involve measurement of basic fog level, speed and average gradient made at 1째 C intervals of temperature. The range of temperature measurement depends on the type of chemistry in use, whether cold or hot developer. These three measurements: fog level, speed, and average gradient, should then be plotted against temperature and compared with the manufacturer's supplied figures.

Charlie Chong/ Fion Zhang

Chapter 10: Viewing Radiographs Radiographs (developed film exposed to x-ray or gamma radiation) are generally viewed on a light-box. However, it is becoming increasingly common to digitize radiographs and view them on a high resolution monitor.

Proper viewing conditions are very important when interpreting a radiograph.

The viewing conditions can enhance or degrade the subtle details of radiographs.

Viewing Radiographs Before beginning the evaluation of a radiograph, the viewing equipment and area should be considered. The area should be clean and free of distracting materials. Magnifying aids, masking aids, and film markers should be close at hand. Thin cotton gloves should be available and worn to prevent fingerprints on the radiograph. Ambient light levels should be low. Ambient light levels of less than 2 fc are often recommended, but subdued lighting, rather than total darkness, is preferable in the viewing room. The brightness of the surroundings should be about the same as the area of interest in the radiograph. Room illumination must be arranged so that there are no reflections from the surface of the film under examination.

Charlie Chong/ Fion Zhang

Film viewers should be clean and in good working condition. There are four groups of film viewers. These include: strip viewers, area viewers, spot viewers, and a combination of spot and area viewers. Film viewers should provide a source of defused, adjustable, and relativity cool light as heat from viewers can cause distortion of the radiograph. A film having a measured density of 2.0 will allow only 1.0 percent of the incident light to pass. A film containing a density of 4.0 will allow only 0.01 percent of the incident light to pass. With such low levels of light passing through the radiograph the delivery of a good light source is important.

The radiographic process should be performed in accordance with a written procedure or code, or as required by contractual documents. The required documents should be available in the viewing area and referenced as necessary when evaluating components. Radiographic film quality and acceptability, as required by the procedure, should first be determined.

Charlie Chong/ Fion Zhang

It should be verified that the radiograph was produced to the correct density on the required film type, and that it contains the correct identification information. It should also be verified that the proper image quality indicator was used and that the required sensitivity level was met. Next, the radiograph should be checked to ensure that it does not contain processing and handling artifacts that could mask discontinuities or other details of interest. The technician should develop a standard process for evaluating the radiographs so that details are not overlooked.

Once a radiograph passes these initial checks it is ready for interpretation.

Radiographic film interpretation is an acquired skill combining, visual acuity with knowledge of materials, manufacturing processes, and their associated discontinues. If the component is inspected while in service, an understanding of applied loads and history of the component is helpful. A process for viewing radiographs, left to right top to bottom etc., is helpful and will prevent overlooking an area on the radiograph. This process is often developed over time and individualized. One part of the interpretation process, sometimes overlooked, is rest. The mind as well as the eyes need to occasionally rest when interpreting radiographs.

Charlie Chong/ Fion Zhang

When viewing a particular region of interest, techniques such as using a small light source and moving the radiograph over the small light source, or changing the intensity of the light source will help the radiographer identify relevant indications. Magnifying tools should also be used when appropriate to help identify and evaluate indications. Viewing the actual component being inspected is very often helpful in developing an understanding of the details seen in a radiograph.

Interpretation of radiographs is an acquired skill that is perfected over time.

By using the proper equipment and developing consistent evaluation processes, the interpreter will increase his or her probability of detecting defects.

Charlie Chong/ Fion Zhang

Chapter 11: Contrast and Definition The first subjective criteria for determining radiographic quality is radiographic contrast. Essentially, radiographic contrast is the degree of density difference between adjacent areas on a radiograph.

It is entirely possible to radiograph a particular subject and, by varying factors, produce two radiographs possessing entirely different contrast levels. With an x-ray source of low kilovoltage, we see an illustration of extremely high radiographic contrast, that is, density difference between the two adjacent areas (A and B) is high. It is essential that sufficient contrast exist between the defect of interest and the surrounding area. There is no viewing technique that can extract information that does not already exist in the original radiograph.

With an x-ray source of high kilovoltage, we see a sample of relatively low radiographic contrast, that is, the density difference between the two adjacent areas (A and B) is low.

Charlie Chong/ Fion Zhang

Radiographic Contrast

Charlie Chong/ Fion Zhang

Definition Besides radiographic contrast as a subjective criteria for determining radiographic quality, there exists one other, radiographic detail. Essentially, radiographic definition is the abruptness of change in going from one density to another. For example, it is possible to radiograph a particular subject and, by varying certain factors, produce two radiographs which possess different degrees of definition.

In the example to the left, a two-step step tablet with the transition from step to step represented by Line BC is quite sharp or abrupt. Translated into a radiograph, we see that the transition from the high density to the low density is abrupt. The Edge Line BC is still a vertical line quite similar to the step tablet itself. We can say that the detail portrayed in the radiograph is equivalent to physical change present in the step tablet. Hence, we can say that the imaging system produced a faithful visual reproduction of the step table. It produced essentially all of the information present in the step tablet on the radiograph.

Charlie Chong/ Fion Zhang

In the example on the right, the same two-step step tablet has been radiographed. However, here we note that, for some reason, the imaging system did not produce a faithful visual reproduction. The Edge Line BC on the step tablet is not vertical. This is evidenced by the gradual transition between the high and low density

Charlie Chong/ Fion Zhang

areas on the radiograph. The edge definition or detail is not present because of certain factors or conditions which exist in the imaging system.

In review, it is entirely possible to have radiographs with the following qualities: ■ Low contrast and poor detail ■ High contrast and poor definition ■ Low contrast and good definition ■ High contrast and good definition One must bear in mind that radiographic contrast and definition are not dependent upon the same set of factors. If detail in a radiograph is originally lacking, then attempts to manipulate radiographic contrast will have no effect on the amount of detail present in that radiograph

Charlie Chong/ Fion Zhang

Chapter 12: Radiographic Density Film speed, gradient, and graininess are all responsible for the performance of the film during exposure and processing. As these combine with processing variables a final product or the radiograph is produced. In viewing the radiograph, requirements have been established for acceptable radiographs in industry. The density of a radiograph in industry will determine if further viewing is possible.

Density considerations date back to early day radiography. Hurder and Drifield have been credited with developing much of the early information on the characteristic curve and density of a radiograph. Codes and standards will typically require densities of a radiograph to be maintained between 1.8 to 4.0 H&D (Hurder and Drifield) for acceptable viewing. As density increases, contrast will also increase.

Charlie Chong/ Fion Zhang

This is true above 4.0 H&D, however as density reaches 4.0 H&D an extremely bright viewing light is necessary for evaluation.

Density, technically should be stated "Transmitted Density" when associated with transparent-base film. This density is the log of the intensity of light incident on the film to the intensity of light transmitted through the film. A density reading of 2.0 H&D is the result of only 1 percent of the transmitted light reaching the sensor. At 4.0 H&D only 0.01% of transmitted light reaches the far side of the film.

Charlie Chong/ Fion Zhang

Chapter 13: Controlling Radiographic Quality One of the methods of controlling the quality of a radiograph is through the use of image quality indicators (IQI). IQIs provide a means of visually informing the film interpreter of the contrast sensitivity and definition of the radiograph. The IQI indicates that a specified amount of material thickness change will be detectable in the radiograph, and that the radiograph has a certain level of definition so that the density changes are not lost due to unsharpness. Without such a reference point, consistency and quality could not be maintained and defects could go undetected.

Image quality indicators take many shapes and forms due to the various codes or standards that invoke their use. In the United States two IQI styles are prevalent; the placard, or hole-type and the wire IQI. IQIs comes in a variety of material types so that one with radiation absorption characteristics similar to the material being radiographed can be used.

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

Hole-Type IQIs ASTM Standard E1025 gives detailed requirements for the design and material group classification of hole-type image quality indicators. E1025 designates eight groups of shims based on their radiation absorption characteristics. A notching system is incorporated into the requirements allowing the radiographer to easily determine if the penetrameter is the correct material type for the product. The thickness in thousands of an inch is noted on each pentameter by a lead number 0.250 to 0.375 inch wide depending on the thickness of the shim. Military or Government standards require a similar penetrameter but use lead letters to indicate the material type rather than notching system as shown on the left in the image above.

Image quality levels are typically designated using a two part expression such as 2-2T. The first term refers to the IQI thickness expressed as a percentage of the region of interest of the part being inspected. The second term in the expression refers to the diameter of the hole that must be revealed and it is expressed as a multiple of the IQI thickness. Therefore, a 2-2T call-out would mean that the shim thickness should be two percent of material thickness and that a hole that is twice the IQI thickness must be detectable on the radiograph. This presentation of a 2-2T IQI in the radiograph verifies Charlie Chong/ Fion Zhang

that the radiographic technique is capable of showing a material loss of 2% in the area of interest.It should be noted that even if 2-2T sensitivity is indicated on a radiograph, a defect of the same diameter and material loss may not be visible. The holes in the penetrameter represent sharp boundaries, and a small thickness change. Discontinues within the part may contain gradual changes, and are often less visible. The penetrameter is used to indicate quality of the radiographic technique and not intended to be used as a measure of size of cavity that can be located on the radiograph.

Charlie Chong/ Fion Zhang

Wire Penetrameters ASTM Standard E747 covers the radiographic examination of materials using wire penetrameters (IQIs) to control image quality. Wire IQIs consist of a set of six wires arranged in order of increasing diameter and encapsulated between two sheets of clear plastic. E747 specifies four wire IQIs sets, which control the wire diameters. The set letter (A, B, C or D) is shown in the lower right corner of the IQI. The number in the lower left corner indicates the material group. The same image quality levels and expressions (i.e. 2-2T) used for hole-type IQIs are typically also used for wire IQIs. The wire sizes that correspond to various hole-type quality levels can be found in a table in E747 or can be calculated using the following formula.

Where: F = 0.79 (constant form factor for wire) D = wire diameter (mm or inch) L = 7.6 mm or 0.3 inch (effective length of wire) T = Hole-type IQI thickness (mm or inch) H = Hole-type IQI hole diameter (mm or inch) Charlie Chong/ Fion Zhang

Placement of IQIs IQIs should be placed on the source side of the part over a section with a material thickness equivalent to the region of interest. If this is not possible, the IQI may be placed on a block of similar material and thickness to the region of interest. When a block is used, the IQI should the same distance from the film as it would be if placed directly on the part in the region of interest. The IQI should also be placed slightly away from the edge of the part so that atleast three of its edges are visible in the radiograph.

Charlie Chong/ Fion Zhang

Chapter 14: Exposure Calculations Properly exposing a radiograph is often a trial and error process, as there are many variables that affect the final radiograph. In this section we make the assumptions of a generic (and fixed characteristic) x-ray source, fixed film type, and fixed quality of development.

The applet below estimates the density of the radiograph based on material, thickness, geometry, energy (voltage), current, and, of course, time. The effect of the energy and the physical setup are shown by looking at the film density after exposure. It should be noted that the applet will differ considerably from industrial x-ray configurations, and is designed for demonstration of variables in an x-ray system.

Charlie Chong/ Fion Zhang

Chapter 15: Radiograph Interpretation - Welds In addition to producing high quality radiographs, the radiographer must also be skilled in radiographic interpretation. Interpretation of radiographs takes place in three basic steps which are (1) detection, (2) interpretation, and (3) evaluation. All of these steps make use of the radiographer's visual acuity.

Visual acuity is the ability to resolve a spatial pattern in an image. The ability of an individual to detect discontinuities in radiography is also affected by the lighting condition in the place of viewing, and the experience level for recognizing various features in the image. The following material was developed to help students develop an understanding of the types of defects found in weldments and how they appear in a radiograph.

Discontinuities Discontinuities are interruptions in the typical structure of a material. These interruptions may occur in the base metal, weld material or "heat affected" zones. Discontinuities, which do not meet the requirements of the codes or specification used to invoke and control an inspection, are referred to as defects.

Charlie Chong/ Fion Zhang

General Welding Discontinuities The following discontinuities are typical of all types of welding.

Cold lap is a condition where the weld filler metal does not properly fuse with the base metal or the previous weld pass material (interpass cold lap). The arc does not melt the base metal sufficiently and causes the slightly molten puddle to flow into base material without bonding.

Charlie Chong/ Fion Zhang

Porosity is the result of gas entrapment in the solidifying metal. Porosity can take many shapes on a radiograph but often appears as dark round or irregular spots or specks appearing singularly, in clusters or rows. Sometimes porosity is elongated and may have the appearance of having a tail This is the result of gas attempting to escape while the metal is still in a liquid state and is called wormhole porosity. All porosity is a void in the material it will have a radiographic density more than the surrounding area.

Charlie Chong/ Fion Zhang

Cluster porosity is caused when flux coated electrodes are contaminated with moisture. The moisture turns into gases when heated and becomes trapped in the weld during the welding process. Cluster porosity appear just like regular porosity in the radiograph but the indications will be grouped close together.

Charlie Chong/ Fion Zhang

Slag inclusions are nonmetallic solid material entrapped in weld metal or between weld and base metal. In a radiograph, dark, jagged asymmetrical shapes within the weld or along the weld joint areas are indicative of slag inclusions.

Charlie Chong/ Fion Zhang

Incomplete penetration (IP) or lack of penetration (LOP) occurs when the weld metal fails to penetrate the joint. It is one of the most objectionable weld discontinuities. Lack of penetration allows a natural stress riser from which a crack may propagate. The appearance on a radiograph is a dark area with well-defined, straight edges that follows the land or root face down the center of the weldment.

Charlie Chong/ Fion Zhang

Incomplete fusion is a condition where the weld filler metal does not properly fuse with the base metal. Appearance on radiograph: usually appears as a dark line or lines oriented in the direction of the weld seam along the weld preparation or joining area.

Charlie Chong/ Fion Zhang

Internal concavity or suck back is condition where the weld metal has contracted as it cools and has been drawn up into the root of the weld. On a radiograph it looks similar to lack of penetration but the line has irregular edges and it is often quite wide in the center of the weld image.

Charlie Chong/ Fion Zhang

Internal or root undercut is an erosion of the base metal next to the root of the weld. In the radiographic image it appears as a dark irregular line offset from the centerline of the weldment. Undercutting is not as straight edged as LOP because it does not follow a ground edge.

Charlie Chong/ Fion Zhang

External or crown undercut is an erosion of the base metal next to the crown of the weld. In the radiograph, it appears as a dark irregular line along the outside edge of the weld area.

Charlie Chong/ Fion Zhang

Offset or mismatch are terms associated with a condition where two pieces being welded together are not properly aligned. The radiographic image is a noticeable difference in density between the two pieces. The difference in density is caused by the difference in material thickness. The dark, straight line is caused by failure of the weld metal to fuse with the land area.

Charlie Chong/ Fion Zhang

Inadequate weld reinforcement is an area of a weld where the thickness of weld metal deposited is less than the thickness of the base material. It is very easy to determine by radiograph if the weld has inadequate reinforcement, because the image density in the area of suspected inadequacy will be more (darker) than the image density of the surrounding base material.

Charlie Chong/ Fion Zhang

Excess weld reinforcement is an area of a weld that has weld metal added in excess of that specified by engineering drawings and codes. The appearance on a radiograph is a localized, lighter area in the weld. A visual inspection will easily determine if the weld reinforcement is in excess of that specified by the engineering requirements.

Charlie Chong/ Fion Zhang

Cracks can be detected in a radiograph only when they are propagating in a direction that produces a change in thickness that is parallel to the x-ray beam. Cracks will appear as jagged and often very faint irregular lines.

Cracks can sometimes appear as "tails" on inclusions or porosity.

Charlie Chong/ Fion Zhang

Discontinuities in TIG welds The following discontinuities are peculiar to the TIG welding process. These discontinuities occur in most metals welded by the process including aluminum and stainless steels. The TIG method of welding produces a clean homogeneous weld which when radiographed is easily interpreted.

Tungsten inclusions. Tungsten is a brittle and inherently dense material used in the electrode in tungsten inert gas welding. If improper welding procedures are used, tungsten may be entrapped in the weld.

Radiographically, tungsten is more dense than aluminum or steel; therefore, it shows as a lighter area with a distinct outline on the radiograph.

Charlie Chong/ Fion Zhang

Oxide inclusions are usually visible on the surface of material being welded (especially aluminum). Oxide inclusions are less dense than the surrounding materials and, therefore, appear as dark irregularly shaped discontinuities in the radiograph.

Charlie Chong/ Fion Zhang

Discontinuities in Gas Metal Arc Welds (GMAW) The following discontinuities are most commonly found in GMAW welds.

Whiskers are short lengths of weld electrode wire, visible on the top or bottom surface of the weld or contained within the weld. On a radiograph they appear as light, "wire like" indications.

Burn-Through results when too much heat causes excessive weld metal to penetrate the weld zone. Often lumps of metal sag through the weld creating a thick globular condition on the back of the weld. These globs of metal are referred to as icicles. On a radiograph, burn through appears as dark spots, which are often surrounded by light globular areas (icicles).

Charlie Chong/ Fion Zhang

Chapter 16: Radiograph Interpretation Castings The major objective of radiographic testing of castings is the disclosure of defects that adversely affect the strength of the product. Casting are a product form that often receive radiographic inspection since many of the defects produced by the casting process are volumetric in nature and, thus, relatively easy to detect with this method. These discontinuities of course, are related to casting process deficiencies, which, if properly understood, can lead to accurate accept-reject decisions as well as to suitable corrective measures. Since different types and sizes of defects have different effects of the performance of the casting, it is important that the radiographer is able to identify the type and size of the defects. ASTM E155, Standard for Radiographs of castings has been produced to help the radiographer make a better assessment of the defects found components. The castings used to produce the standard radiographs have been destructively analyzed to confirm the size and type of discontinuities present. The following is a brief description of the most common discontinuity types included in existing reference radiograph documents (in graded types or as single illustrations).

Charlie Chong/ Fion Zhang

RADIOGRAPHIC INDICATIONS FOR CASTINGS Gas porosity or blow holes are caused by accumulated gas or air which is trapped by the metal. These discontinuities are usually smooth-walled rounded cavities of a spherical, elongated or flattened shape. If the sprue is not high enough to provide the necessary heat transfer needed to force the gas or air out of the mold, the gas or air will be trapped as the molten metal begins to solidify. Blows can also be caused by sand that is too fine, too wet, or by sand that has a low permeability so that gas can't escape. Too high a moisture content in the sand makes it difficult to carry the excessive volumes of water vapor away from the casting. Another cause of blows can be attributed to using green ladles, rusty or damp chills and chaplets.

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

Sand inclusions and dross are nonmetallic oxides, appearing on the radiograph as irregular, dark blotches. These come from disintegrated portions of mold or core walls and/or from oxides (formed in the melt) which have not been skimmed off prior to introduction of the metal into the mold gates. Careful control of the melt, proper holding time in the ladle and skimming of the melt during pouring will minimize or obviate this source of trouble.

Charlie Chong/ Fion Zhang

Shrinkage is a form of discontinuity that appears as dark spots on the radiograph. Shrinkage assumes various forms but in all cases it occurs because molten metal shrinks as it solidifies, in all portions of the final casting.

Shrinkage is avoided by making sure that the volume of the casting is adequately fed by risers which sacrificially retain the shrinkage. Shrinkage can be recognized in a number of characteristic by varying appearances on radiographs. There are at least four types: (1) cavity; (2) dendritic; (3) filamentary; and (4) sponge types. Some documents designate these types by numbers, without actual names, to avoid possible misunderstanding.

Cavity shrinkage appears as areas with distinct jagged boundaries. It may be produced when metal solidifies between two original streams of melt, coming from opposite directions to join a common front; cavity shrinkage usually occurs at a time when the melt has almost reached solidification temperature and there is no source of supplementary liquid to feed possible cavities.

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

Dendritic shrinkage is a distribution of very fine lines or small elongated cavities that may vary in density and are usually unconnected.

Filamentary shrinkage usually occurs as a continuous structure of connected lines or branches of variable length, width and density, or occasionally as a network.

Charlie Chong/ Fion Zhang

Sponge shrinkage shows itself as areas of lacy texture with diffuse outlines, generally toward the mid-thickness of heavier casting sections. Sponge shrinkage may be dendritic or filamentary shrinkage; filamentary sponge shrinkage appears more blurred because it is projected through the relatively thick coating between the discontinuities and the film surface.

Charlie Chong/ Fion Zhang

Cracks are thin (straight or jagged) linearly disposed discontinuities that occur after the melt has solidified. They generally appear singly and originate at casting surfaces.

Cold shuts generally appear on or near a surface of cast metal as a result of two streams of liquid meeting and failing to unite. They may appear on a radiograph as cracks or seams with smooth or rounded edges.

Charlie Chong/ Fion Zhang

Inclusions are nonmetallic materials in a supposedly solid metallic matrix.

They may be less or more dense than the matrix alloy and will appear on the radiograph, respectively, as darker or lighter indications. The latter type is more common in light metal castings.

Charlie Chong/ Fion Zhang

Core shift shows itself as a variation in section thickness, usually on radiographic views representing diametrically opposite portions of cylindrical casting portions.

Charlie Chong/ Fion Zhang

Hot tears are linearly disposed indications that represent fractures formed in a metal during solidification because of hindered contraction. The latter may occur due to overly hard (completely unyielding) mold or core walls. The effect of hot tears, as a stress concentration, is similar to that of an ordinary crack; how tears are usually systematic flaws. If flaws are identified as hot tears in larger runs of a casting type, they may call for explicit improvements in technique.

Misruns appear on the radiograph as prominent dense areas of variable dimensions with a definite smooth outline. They are mostly random in occurrence and not readily eliminated by specific remedial actions in the process.

Charlie Chong/ Fion Zhang

Mottling is a radiographic indication that appears as an indistinct area of more or less dense images. The condition is a diffraction effect that occurs on relatively vague, thin-section radiographs, most often with austenitic stainless steel. Mottling is caused by interaction of the object's grain boundary material with low-energy X-rays (300 kV or lower). Inexperienced interpreters may incorrectly consider mottling as indications of unacceptable casting flaws.

Even experienced interpreters often have to check the condition by reradiography from slightly different source-film angles. Shifts in mottling are then very pronounced, while true casting discontinuities change only slightly in appearance.

Charlie Chong/ Fion Zhang

Radiographic Indications for Casting Repair Welds Most common alloy castings require welding either in upgrading from defective conditions or in joining to other system parts. It is mainly for reasons of casting repair that these descriptions of the more common weld defects are provided here. The terms appear as indication types in ASTM E390. For additional information, see the Nondestructive Testing Handbook, Volume 3, Section 9 on the "Radiographic Control of Welds."

Slag is nonmetallic solid material entrapped in weld metal or between weld material and base metal. Radiographically, slag may appear in various shapes, from long narrow indications to short wide indications, and in various densities, from gray to very dark.

Porosity is a series of rounded gas pockets or voids in the weld metal, and is generally cylindrical or elliptical in shape.

Undercut is a groove melted in the base metal at the edge of a weld and left unfilled by weld metal. It represents a stress concentration that often must be corrected, and appears as a dark indication at the toe of a weld.

Charlie Chong/ Fion Zhang

Incomplete penetration, as the name implies, is a lack of weld penetration through the thickness of the joint (or penetration which is less than specified).

It is located at the center of a weld and is a wide, linear indication.

Incomplete fusion is lack of complete fusion of some portions of the metal in a weld joint with adjacent metal; either base or previously deposited weld metal. On a radiograph, this appears as a long, sharp linear indication, occurring at the centerline of the weld joint or at the fusion line.

Melt-through is a convex or concave irregularity (on the surface of backing ring, strip, fused root or adjacent base metal) resulting from complete melting of a localized region but without development of a void or open hole. On a radiograph, melt-through generally appears as a round or elliptical indication.

Burn-through is a void or open hole into a backing ring, strip, fused root or adjacent base metal.

Charlie Chong/ Fion Zhang

Arc strike is an indication from a localized heat-affected zone or a change in surface contour of a finished weld or adjacent base metal. Arc strikes are caused by the heat generated when electrical energy passes between surfaces of the finished weld or base metal and the current source.

Weld spatter occurs in arc or gas welding as metal particles which are expelled during welding and which do not form part of the actual weld: weld spatter appears as many small, light cylindrical indications on a radiograph.

Tungsten inclusion is usually denser than base-metal particles. Tungsten inclusions appear most linear, very light radiographic images; accept/reject decisions for this defect are generally based on the slag criteria.

Oxidation is the condition of a surface which is heated during welding, resulting in oxide formation on the surface, due to partial or complete lack of purge of the weld atmosphere. Also called sugaring.

Charlie Chong/ Fion Zhang

Root edge condition shows the penetration of weld metal into the backing ring or into the clearance between backing ring or strip and the base metal. It appears in radiographs as a sharply defined film density transition.

Root undercut appears as an intermittent or continuous groove in the internal surface of the base metal, backing ring or strip along the edge of the weld root.

Charlie Chong/ Fion Zhang

Real-time Radiography Real-time radiography (RTR), or real-time radioscopy, is a nondestructive test (NDT) method whereby an image is produced electronically rather than on film so that very little lag time occurs between the item being exposed to radiation and the resulting image. In most instances, the electronic image that is viewed, results from the radiation passing through the object being inspected and interacting with a screen of material that fluoresces or gives off light when the interaction occurs. The fluorescent elements of the screen form the image much as the grains of silver form the image in film radiography.

The image formed is a "positive image" since brighter areas on the image indicate where higher levels of transmitted radiation reached the screen. This image is the opposite of the negative image produced in film radiography. In other words, with RTR, the lighter, brighter areas represent thinner sections or less dense sections of the test object.

Charlie Chong/ Fion Zhang

Real-time radiography is a well-established method of NDT having applications in automotive, aerospace, pressure vessel, electronic, and munition industries, among others. The use of RTR is increasing due to a reduction in the cost of the equipment and resolution of issues such as the protecting and storing digital images. Since RTR is being used increasingly more, these educational materials were developed by the North Central Collaboration for NDT Education (NCCE) to introduce RTR to NDT technician students.

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

Read More: https://www.nde-ed.org/TeachingResources/teachingresources.htm