Exceptional Performance, High Temperature, Ceramic Repair Compound
AbraCor 5 Hi-Temp ®
( With Kevlar®)
COATING • High performance polymer for in-situ repairs, requiring no special tools • Fine silicon carbide particles enhance wear properties • Angular aluminum oxide particles increase resistance to abrasion and erosion • Uniform distribution of interlocking Kevlar fibers add toughness and impact resistance
AbraCor Formula 5 Hi-Temp with Kevlar is a high performance polymer that provides resistance to erosion and abrasion while ensuring good adhesion to a wide variety of metal and rigid non-metal surface. It is comprised of a two-part epoxy system consisting of a hardener and a resin. When mixed, the components react and cure to form a wear resistant coating. AbraCor Formula 5 Hi-Temp is composed of four primary ingredients; a high performance polymer, silicon carbide particles, aluminum oxide particles and interlocking Kevlar fibers.
· Rebuild worn areas on pumps and impellers · Line chutes, elbows and piping sections that are used to convey abrasive materials (coal, cement, etc.) · Form a wear face on fan blades and fan housings · Restore screw flights to dimension · Cast wear plate/wear pad
AbraCor Formula 5 Hi-Temp has been formulated to allow application in-situ, with no special tools and without the need for additional heat. Plus it is suitable for use on both new and worn parts. It can be “cast” into irregular shapes for use as wear pad / wear plate. Abracor 5 Hi-Temp is excellent for applications between 150°F -400°F (65°C-200°C).
APPLICATION PROCEDURE: 1. Remove oil, grease and scale from the surface to be coated. To ensure optimum adhesion, roughen by grit blasting to achieve a 0.002-0.003 inch profile. For small areas roughening with a grinding wheel or coarse sandpaper is acceptable. 2. For large applications combine the entire contents of resin and hardener, then mix until a uniform, streak-free, Light gray color is achieved. Use mechanical mixing equipment to ensure uniformity. For small repairs combine a ratio of four parts resin to one part hardener by volume and mix thoroughly. 3. Spread evenly over the surface with a trowel. Press the material into cracks and voids to eliminate air bubbles. Use a dragging motion with light pressure on the tool to achieve a smooth surface texture. Pot life is about 25 minutes at 75°F (approx. 24°C). 4. AbraCor 5 Hi-Temp requires a curing temperature between 150° and 350°F (65°C and 177°C). To achieve this temperature, the coated part should be heated indirectly unless the curing temperature will be reached during service start-up.
TECHNICAL DATA: PHYSICAL PROPERTY
Hardness Shore D: Compressive Strength: Lap Shear: Shrinkage: Machinable: Speciﬁc Gravity:
90 17,000 psi 3,600 psi Passed No 0.074 lb/in 3
Max. Operating Temp.:
400°F (approx. 200°C)
ASTM TEST D 695 D 1002 C 881 D 792 -
PROCESS PARAMETERS: Color, mixed:
Mixing ratio by volume:
4 resin : 1 hardener
Pot life at 75°F: (approx. 24°C)
Return to service:
3 - 4 hours
100% cure @ 150°F: 100% cure @ 350°F:
2 hours 30 minutes
2.66 lb per ft 2@ ¼” thick 13.5 in3 per lb
Super thick paste
COVERAGE: 5 lb Kit: 20 lb Kit:
1.9 ft 2@ ¼” (6.4mm) thick 7.6 ft 2@ ¼” (6.4mm) thick
YOUR RESOURCE FOR PROTECTION, REPAIR AND JOINING SOLUTIONS Eutectic Corporation N94 W14355 Garwin Mace Drive Menomonee Falls, WI 53051 USA P 800-558-8524 • F 262-255-5542 www.eutecticusa.com
Eutectic Canada 428, rue Aime Vincent Vaudreuil-Dorion, Quebec J7V 5V5 Phone: (800) 361-9439 Fax: (514) 695-8793 www.eutectic-na.com
Eutectic Mexico KM 36.5 Autopista Mexico-Quertaro 54730 Cautitlan-Izcalli Estado de Mexico, Mexico Phone: 011 (52) 55-5872-1111 e-mail: firstname.lastname@example.org
Statement of Liability: Due to variations inherent in speciﬁc applications, the technical information contained herein, including any information as to suggested product applications or results, is presented without representation or warranty, expressed or implied. Without limitation, there are no warranties of merchantability or of ﬁtness for a particular purpose. Each process and application must be fully evaluated by the user in all respects, including suitability, compliance with applicable law and non-infringement of the rights of others, and Eutectic Corporation and its afﬁliates shall have no liability in respect thereof. AB5HT 10-09 © 2008, Eutectic Corporation, ® Reg. T.M., Printed in the U.S.A.