THE ULTIMATE GFRP REINFORCING PRODUCTS
STRONG AND DURABLE Table of Contents Page Page # # 22 Product Applications History and Overview 33- -46 MateenBolt™ MateenBolt™ 57 -- 610 MateenBar™ MateenBar™ 7 - -814 MateenDowel™ 11 MateenDowel™ 915 - 10 Specifications -16 Suggested Specifications 1.360.859.3170
www.mateenfrp.com
mateen@sigmadg.com
2
STRONG AND DURABLE History and Overview In 1985 Pultron worked with DuPont, Australia to develop a reinforcement system that addressed the shortfalls of steel. In 1990 Pultron worked in conjunction with BHP to develop a world first technology combining pultrusion and extrusion. The resulting product was a reinforcement system to stabilize high movement rock & coal seams, dramatically improving mine safety in difficult geotechnical conditions. Since then Pultron has worked with various companies, developing FRP reinforcement specific to their requirements. Ongoing R&D projects ensure that Pultron is at the leading edge of technology. The Mateen product line is the ideal product line that delivers high performing corrosion resistant reinforcement suited perfectly for many applications where steel falls short. Sigma DG Corporation partnered with Pultron Composites LTD in 2010 to bring the Mateen product line to the Western Hemisphere. Since the partnership was formed, the Mateen brand has expanded from MateenBar™ to also include the MateenDowel™ and MateenBolt™.
4
cutable • non-corrosive • non-magnetic • non-conductive • high strength • light weight 22mm
Permanent Bolts
Temporary Bolts
25mm
32mm
32mm Hollow
kip
kN
kip
kN
kip
kN
kip
kN
Guaranteed Tensile
>53
>235
>63
>280
>97
>430
>76
>340
Shear
>12
>54
>15
>65
>24
>108
>20
>90
Nut Termination
>14.5
>65
>20
>90
>34
>150
>34
>150
Working Area
0.44in2
285mm2
0.60in2
385mm2
1.00in2
645mm2
0.82in2
532mm2
Elastic Modulus*
>7.7 msi
>53 GPa
>7.7 msi
>53 GPa
>7.7 msi
>53 GPa
>7.7 msi
>53 GPa
Guaranteed Tensile
>48
>215
>58
>260
>90
>400
Shear
>11
>50
>13
>58
>22
>100
Nut Termination
>14.5
>65
>20
>90
>34
>150
Working Area
0.44in2
285mm2
0.60in2
385mm2
1.00in2
645mm2
Elastic Modulus*
>7.7 msi
>53 GPa
>7.7 msi
>53 GPa
>7.7 msi
>53 GPa
*Elastic Modulus is based on the working area of the bolt
The difference in performance (both mechanical and durability properties) is attributable to the resin and glass systems used for each bolt type. The permanent MateenBolt™ is made from a high durability epoxy backboned resin matrix and E-CR glass making it perfect for long term installations and/or corrosive environments. The temporary bolt is made with value in mind for the end user not needing a highly durable bolt, but a cutable bolt. To accomplish this, the temporary bolt uses a high grade polyester blended resin and e-glass which is suitable for installations which will last less than 2 years.
5
cutable • non-corrosive • non-magnetic • non-conductive • high strength • light weight
Temporary Cutable bolts for temporary ground support NATM / SEM / Lunardi Tunneling method ground support Temporary coil rod for concrete form ties
Permanent used as primary roof support in high h2s environments such as combined sewer overflow (CSO) tunnels in lieu of double corrosion protected bolts. soil nails used in corrosive (alkali or acidic) soils as a replacement for galvanized, epoxy, stainless, or double corrosion protected bolt hollow bolt can be used as a corrosion resistant self drilling bolt in loose soils
has been installed in the following types of mines… coal
gold
salt
lead
potash
zinc cobalt
MateenBolt™ Advantages MateenBolt™ was designed not to be just another fiberglass rock dowel. Pultron purposely created a one of a kind grinding machine to precision machine the threads on the MateenBolt giving it the strongest composite nut pull off strength in the world. To further separate MateenBolt™ from the competition, these bolts are available fully threaded up to 40 feet in length. This allows the cut pieces to still have useable threads!
Mining Product Line Up
MateenBar™ is formulated and manufactured to the edge of the theoretical limits of the glass and resins from which it is made. MateenBar™ is made from corrosion resistant E-CR glass supplied by Owens Corning and an epoxy backboned resin matrix making it highly durable in the most corrosive environments. All Mateen FRP is manufactured to the highest quality standards under ISO 9001.
8
cutable • non-corrosive • non-magnetic • non-conductive • high strength • light weight Tensile Strength / Working Area Nominal Diameter mm
#
Guaranteed Tensile
Working Area
MPa
mm2
ksi
6
900
21
8
885
41
10
3
12
860
125
820
67
in2
based on working area
0.10
Flexural Strength >900 MPa / >130 ksi Transverse Shear >150 MPa / >22 ksi
Glass Content minimum 75% by weight
Bond Strength 16 MPa / 2.3 ksi
Compressive Strength >400 MPa / >58 ksi
Short Beam Shear >50 MPa / >7.25 ksi
Glass Transition Temp 110º C / 230º F
99
4
800
116
137
0.21
16
5
780
113
182
0.28
760
Moisture Uptake <0.1% CTE: /ºC Longitudinal - 7.2x10-6 Transverse - 22x10-6
14
18
E-Modulus >53 GPa / >7,700 ksi
232
20
6
760
110
290
0.45
22
7
750
109
355
0.55
25
8
720
104
458
0.71
31.4
9
670
97
735
1.14
37.4
11
650
94
1052
1.63
9
cutable • non-corrosive • non-magnetic • non-conductive • high strength • light weight Corrosion Resistance bridge deck and railing concrete reinforcement through AASHTO. waste water treatment plants architectural precast (prevent rust stains) reinforce old masonry buildings seawall reinforcement flood control dike reinforcement water or soil submerged concrete structures continuously reinforced concrete pavement (CRCP) slab on grade and concrete wall reinforcement in: highly corrosive environments gas and oil pipeline pads
High Voltage / Electromagnetic Fields aluminum smelter concrete reinforcement slab on grade and concrete wall reinforcement in: electrical utility pads electrical trolly lines gas and oil pipeline pads - to protect from stray current wind turbine pads MRI facilities
Temporary Installations soft-eye openings for TBM launch and reception boxes - slurry walls and/or piles (cassions) consumable rock dowels
Other applications sea piles and marine fenders marina structures precast segmental liners precast concrete pipes
transformer SVC pads
chemical processing plants
MateenBar™ Advantages MateenBar has been perfected by over 25 years of ongoing R&D to perform in the harshest environments. It has superior physical characteristics to most any GFRP made and is produced near the theoretical limits of the resin and glass. MateenBar™ is made from the highest quality epoxy backboned resin matrix and e-cr glass which gives it unparalleled durability and unquestionable quality.
MateenBarâ&#x201E;˘ in substation SVC (static var compensator) pads
prefab rebar mats
MateenBarâ&#x201E;˘ in precast MSE seawall
placed into form
cast into elements
12
non-corrosive • non-magnetic • non-conductive • better fatigue life • light weight • less stress Tested Performance The typical purpose of a smooth dowel is to distribute, resist, and/or transfer shear forces. Because of this, it is critically important to have the highest possible shear strength. The table below compares shear testing of 3 typical GFRP dowel bars from different manufacturers as well as the MateenDowel™. The test of the 3 GFRP dowels from various manufacturers was conducted and published in a 2001 ACI publication by Eddie et al. The MateenDowel™ double shear test was conducted by a 3rd party testing facility.
The MateenDowel™ outperformed the strongest GFRP dowel by 30 percent in double shear testing. For specification language, see page 15.
Dowel Type
Diameter (mm)
# Samples
Double Shear Load (kN)
Shear Strength (MPa)
Standard Deviation
GFRP - 1
38.1
3
244
107
3.8
GFRP - 2
38.1
3
343
150
3.2
GFRP - 3
38.1
3
231
101.3
3.1
MateenDowel™
37.62
8
437
196.6
4.65
13
non-corrosive • non-magnetic • non-conductive • better fatigue life • light weight • less stress Areas of Application
MateenDowels™ in Dowel Bar Retrofit (DBR)
jointed concrete pavement (JCP) dowel bar retrofit (DBR) panel replacement (drill and Dowel) precast panels mechanically stabilized earth (MSE) wall shear pins
MateenDowel™ Advantages MateenDowel™ is a superior corrosion resistant and cost effective dowel as compared to any type of steel dowel currently approved for use today. Additionally, the ability of GFRP to distribute cyclical loading forces more efficiently than steel and a modulus more closely matching concrete, allows the MateenDowel to work in conjunction with the concrete, lowering the overall stresses within the concrete giving joints longer service life.
MateenDowels™ in MSE Retaining Walls Muscat Expressway
MateenDowelsâ&#x201E;˘ installed with a Dowel Bar Insertion (DBI) machine
15
Specifications
Material Specification
Material Specification
Material Specification
GFRP rebar shall be made from Epoxy based vinyl ester resin and e-cr glass. EGlass shall not be allowed.
GFRP Dowels shall be made from epoxy vinyl ester resin and e-cr glass. E-Glass shall not be allowed.
Elastic modulus shall be no less than 7250 ksi or 50 GPa according to ASTM D 7205 and ACI 440.3R-4
Average transverse (double) shear shall be no less than 27.5 ksi or 190 MPa according to ACI 440.3R-4
GFRP Bolts for long term applications shall be made from Epoxy based vinyl ester resin and e-cr glass. E-Glass and polyester resin shall only be allowed for installations less than 2 years in length.
Moisture uptake shall be no greater than 0.1% according to ASTM D 570 - 48 hour method.
Moisture uptake shall be no greater than 0.1% according to ASTM D 570 - 48 hour method.
Glass Transition shall be no less than 110ยบ C according to ASTM E 1640 - 04 (DMTA Method - measured on the storage modulus curve).
Glass Transition shall be no less than 110ยบ C according to ASTM E 1640 - 04 (DMTA Method - measured on the storage modulus curve).
Double shear shall be no less than 29 ksi or 200 MPa for long term bolts and no less than 27.5 ksi or 190 MPa for temporary bolts according to ACI 440.3R-4 Non metallic nut termination shall develop no less than 20,000 lbs for 1 inch bolt, and no less than 35,000 lbs for a 1.25 inch bolt. Strengths confirmed by pull tests. Moisture uptake shall be no greater than 0.1% according to ASTM D 570 - 48 hour method for long term bolting installations. Glass Transition shall be no less than 110ยบ C according to ASTM E 1640-04 (DMTA Method - measured on the storage modulus curve).
Specification Language
16
QC / Mill Certification Requirements TEST WITH EVERY SHIPMENT Incoming Resin (ASTM E 1356)
Diameter (certified vernier)
Glass Content (astm d 3171)
Short Beam Shear Strength (ASTM D 4475)
REQUIREMENTS Enthalpy of reaction and Glass Transition temperature analysis by DSC prior to processing Minimum of 1 per resin batch (may apply to more than one batch of dowel production) As measured from tolerance sheets at 2 hourly checks Glass content check every 2 hours Average and standard deviation derived from production tolerance sheets short beam shear test performed from each product stream every 2 hours
Glass Transition Temperature (ASTM E 1640)
Minimum of 1 test per batch for production runs of less than 10,000 meters, one test per batch is considered
Surface
that the surface is crack free, as per the two hourly tolerance sheet information
Pultron Composites LTD is an ISO certified manufacturing facility
www.mateenfrp.com
360.859.3170 mateen@sigmadg.com All Mateen products have been tested/estimated according to AASHTO , ACI and recommended ASTM methods. Mateen Products are sold subject to Pultronâ&#x20AC;&#x2122;s standard warranty and nothing herein shall expand or extend such warranty. The data contained herein is considered representative of present production and believed to be reliable. Pultron Composites Limited reserves the right to make improvements in the product and process which may result in benefits and/or changes to some physical and mechanical properties.