PROTECTIVE COATING | INNOVATIONS ANTICORROSIVE POWDER COATING PPA 571 Polvere anticorrosiva PPA 571
P
lascoat Systems Limited is the world leader in thermoplastic powder coating for corrosion prevention and metal protection. The company has been producing PPA 571 for almost 20 years; it is one of the most versatile materials available on the market today, able to provide superior resistance to environmental exposure, wear and tear, damage and malicious attack with no effect to its performance and low maintenance requirements. The powder can be applied either by dip coating or by electrostatic spraying like any other powdered paint. The coating forms an impermeable layer on top of the metal substrate that is virtually impenetrable by liquids or gases. Thanks to its insulating properties, it also prevents the formation of cathodic cells necessary for the corrosion to occur. The technology is based on a polyolefin alloy and this imparts exceptional adhesion properties without the need for a primer; the additive package offers excellent resistance to heat and light. Table 1 ISO 7253 Steel
- Scribed
lascoat Systems Limited è leader mondiale nel settore dei rivestimenti con polveri termoplastiche per l’anticorrosione e la protezione dei metalli. L’azienda produce il PPA571 da quasi 20 anni; si tratta di uno dei materiali più versatili attualmente disponibili sul mercato, in grado di assicurare una resistenza superiore all’esposizione ambientale, all’usura, al danneggiamento e agli attacchi vandalici senza alterare le sue performance e i bassi requisiti di manutenzione. La polvere può essere applicata mediante immersione in letto fluido oppure mediante spruzzatura elettrostatica come qualsiasi altra vernice in polvere. Il rivestimento forma uno strato impermeabile sopra al substrato metallico rendendolo praticamente impenetrabile a liquidi o gas. Grazie alle proprietà isolanti, impedisce anche la formazione delle celle catodiche necessarie all’innesco della corrosione. La tecnologia utilizzata, basata su una lega di poliolefine modificate, conferisce eccezionali proprietà di adesione senza necessità di primer; il pacchetto di additivi utilizzati offre un’ottima resistenza al calore e alla luce. Tab. 1
Results after 1000 hours Loss of adhesion less than 10mm from scribe. Under film corrosion 2-3mm No loss of adhesion No loss of adhesion No loss of adhesion
Nebbia salina
Risultati dopo 1000 ore Perdita di adesione inferiore a 10mm dalla traccia. Corrosione sottopellicolare - Non tracciato 2-3mm Alluminio - Tracciato Nessuna perdita di adesione - Non Tracciato Nessuna perdita di adesione Nessuna perdita di adesione
Adesione
EN ISO 4624
Salt Spray
- Unscribed Aluminium - Scribed - Unscribed
Adhesion
EN ISO 4624
15MPa
QUV ASTM G53-77
2000 hrs - No significant change in colour or loss of gloss.
ISO 7253 Acciaio - Tracciato
Degrado da agenti atmosferici
Weathering Florida 45° facing South
P
3 years - No significant change in colour or loss of gloss.
PPA 571 is extremely flexible with an extension to break of more than 800% compared to less than 20% for a typical epoxy or polyester based coating. This confers outstanding edge coverage as well as unequalled resistance to abrasion, chipping and cracking.
QUV ASTM G53-77 Florida 45° verso Sud
15MPa 2000 ore - Nessuna variazione significativa del colore né perdita di lucentezza 3 anni - Nessuna variazione significativa del colore né perdita di lucentezza
PPA 571 è estremamente flessibile con una estensione a rottura superiore all’800% rispetto ad un allungamento inferiore al 20% per un poliestere o un epossidico tipico. Questa caratteristica consente un’eccellente copertura degli spigoli oltre ad un’impareggiabile resistenza all’abrasione, alla scagliatura e alla criccatura.