Tool Base Materials Tool materials Tool categories
C old w orking steels
H ot w orking steels
Maraging steels
3
Service properties
Tool B ase Materials Material N o.
Welding C onsumable Group
Euronorm designation
H ardness / Strength
Electrode
GMA
2R 6 680 S 6055 6080 6804 6806 9025 9080 54306 54425
D O*04 D O*06 D O*13 D O*15 D O*16 D O*53 S D O*55 D O*80 D O*85 D O*329 45303 45351
45301 45303 45305 45318 45351 45353 45355 45507 45654
50-58 HRC 42-56 HRC 42-56 HRC
680 S 6055 54355
D O*02 D O*24 S D O*53 S D O*55
45353 W 45355 W 45507 W
2R 6 3292 6080 6806 54306
D O*13 D O*15 D O*53 S 45301 45303 45351
45301 45303 45351 45353
W W W W
680 S 6055 6800 6804 6817 6865 6899 9025 9060 9080 9120 54304 54355 54425 54668
D O*04 D O*55 D O*60 D O*70 D O*80 D O*84 D O*85 D O*329 45651 45653 45654
45305 45355 45406 45421 45651 45653 45654
W W W W W W W
6055 6865 54355
D O*55 D O*84 45651 45654
1.2067 1.2080 1.2363 1.2379 1.2436 1.2550 1.2601 1.2842
100 C r 6 X 210 C r 12 X 100 C rMoV 5-1 X 155 C rVMo 12-1 X 210 C rW 12 60 WC rV 7 X 165 C rMoV 12 90 MnC rV 8
1.2162 1.2311 1.2713 1.2721 1.2767 1.7140
21 MnC r 5 40 C rMnMo 7 55 Ni C rMoV 6 50 Ni C r 13 X 45 Ni C rMo 4 G 47 C rMn 6
1.2769 1.7218 1.7225
G 45 C rNi Mo 4-2 G 25 C rMo 4 G 42 C rMo 4
1.2082 1.2764 1.7218 1.7225
X X G G
C r 13 C rNi Mo 4 C rMo 4 C rMo 4
800-1000 N/mm2 60 HRC 900-1100 N/mm2 1100-1300 N/mm2
1.2343 1.2344 1.2365 1.2367 1.2567 1.2581 1.2606 1.2662 1.2714 1.2726 1.2731 1.2740 1.2744 1.2678 1.2885 1.2888 1.2713 1.2767
X 38 C rMoV 5-1 X 40 C rMoV 5-1 X 32 C rMoV 3-3 X 38 C rMoV 5-3 X 30 WC rV 5-3 X 30 WC rV 9-3 X 37 C rMoV 5-1 X 30 WC rC oV 9-3 56 Ni C rMoV 6 26 Ni C rMoV 5 X 50 Ni C rWV 13-13 28 Ni C rMoV 10 57 Ni C rMoV 7-7 X 45 C oC rWV 5-5-5 X 32 C rMoC oV 3-3-3 X 20 C oC rWMo 10-9 55 Ni C rMoV 6 X 45 Ni C rMo 4
1400-1700 N/mm2 1400-1750 N/mm2 1500-1800 N/mm2 1400-1600 N/mm2 1200-1700 N/mm2 1400-1790 N/mm2 1500-1800 N/mm2 1200-1500 N/mm2 1500-1800 N/mm2 900-1100 N/mm2 940-1130 N/mm2 1300-1700 N/mm2 1200-1700 N/mm2 1300-1700 N/mm2 1400-1700 N/mm2 1400-1800 N/mm2 1200-1400 N/mm2 1200-1700 N/mm2
2.4982
Ni C r 20 C oMo
1.2779 1.2709 1.2799
X 6 Ni C rTi 26-15 X 3 Ni C oMoTi 18-9-5 X 2 Ni C oMoTi 12-8-8
21 19 25 42
Optimising to R equired Properties
54-58 58-63 56-62 56-62 58-63 54-58 58-62 56-62
HRC HRC HRC HRC HRC HRC HRC HRC
56-60 HRC 1000-1100 N/mm² 52-58 HRC 50-52 HRC 52-56 HRC 54-58 HRC
TIG
W W W W W W W W W
1230 N/mm2 930-1180 N/mm2 55-56 HRC 53-55 HRC
Electrode
MMA
= SMAW
= Shielded Metal Arc Welding
GMA
MIG/MAG
= GMAW
= Gas Metal Arc Welding
TIG
TIG
= GTAW
= Gas Tungsten Arc Welding © 2002 - Castolin Eutectic
45355 W 45651 W 45654 W
For optimum results a “Buttering Layer” may be required. Consult your local Castolin Eutectic Technical Dept.