technology in fast growing areas such as EastTAB. 2 - IMERYS KAOSHINE BB30 TECHNICAL DATA SHEET ern Europe, North Africa and the Scheda tecnica del caolino KaoShine BB30 Middle East. KaoShine BB30 If we take a closer look at the Chemical Analysis (mass %) - Analisi Chimica chemical analysis of KaoShine BB30 (Table 2), the most evident SiO2 47.1 characteristics are its high aluAl2O3 37.6 mina and low chromophore conFe2O3 0.35 tent and consequently high level TiO2 0.56 of whiteness. This means that less K O 0.4 zircon or whitener is needed to 2 achieve the requisite whiteness, Na2O <0,1 hence reducing costs. The second CaO 0.4 notable element is the low levMgO <0,1 el of contaminants, which results L.O.I 13.4 in a decrease in glaze and body defects and an improvement in Particle size analysis – Sedigraph (cumulative mass %) - Analisi Granulometrica < 10 µm 95 the user’s quality yield. Further aspects include the fine particle < 5 µm 87 size, which improves compaction < 2 µm 70 and dry mechanical strength in superwhite per piastrelle e labodies, as well as rheology and suspension in glazes. stre, in particolare in aree produttive in rapida crescita co❱ Ball clays for plasticity and fusibility me l'Europa orientale, il Nord Africa e il Medio Oriente. Ball clays can be used in combination with kaolin in processSe si esamina più da vicino es with less stringent whiteness requirements: 86 < L* body < 88. l'analisi chimica del KaoShiImerys’ FMT and TSMA have been go-to solutions for porcene BB30 (Tab. 2), le caratterilain tile production over the last few decades both in Europe stiche che spiccano sono, da and in overseas markets. With the gradual shift in production un lato, l'alta percentuale di from tiles to large slabs, the requirement for high plasticity allumina e il basso contenuto and pressability of bodies is now more important than ever. di cromofori: questo determiThe two above-mentioned ball clays from Imerys have a very na l’elevata bianchezza conhigh level of plasticity due to their ideal combination of kaosentendo quindi di ridurre la linite, illite and smectite (montmorillonite), which delivers outquantità di zirconio o sbianstanding whiteness and plasticity together with standard fusibility. TAB. 3 - CHEMICAL ANALYSIS OF IMERYS’ BALL CLAY To achieve these Analisi chimica delle ball clay Imerys levels of performance, a conHymod Hymod FMT TSMA Amalia Saphire tent of 5% to 10% Chemical Analysis (mass %) - Analisi Chimica of ball clay in the body composition SiO2 56 62.3 60 60 is sufficient for conAl2O3 30 23.75 26 27 trolling slip viscosFe2O3 1.3 1.54 1.2 1.3 ity. Typically, TSTiO2 0.62 0.58 1.3 1.4 MA clay is used to K O 0.4 0.65 0.25 0.2 increase the dry 2 Na2O 0.7 1.03 0.5 0.3 Modulus of Rupture of less plastic clays CaO 0.89 0.86 2.6 2.2 in standard whiteMgO 0.1 0.15 0.35 0.3 ness porcelain tile L.O.I 9.5 8.63 7.7 8 bodies, while FMT Carbon 0.2 0.16 0.25 0.2 is preferable for inParticle size analysis – Sedigraph (cumulative mass %) Analisi Granulometrica creasing the Modulus of Rupture of > 53 µm 4.9 3.6 1 1.2 white porcelain tile < 2 µm 72 67.75 76 79 or slab bodies in 24.1 23.9 7 7.5 MoR Dried at 100°C (MN m-2) - MoR Essiccato a 100°C association with kaBET (m2.g-1) 27 41 33 34 olins (Table 3). 90 CWR 143/2021 canti e, di conseguenza, i costi. Dall’altro, si noti il basso livello di contaminanti, che si traduce nella riduzione dei difetti di smalto e impasto e in un miglioramento della resa qualitativa. Altri elementi da sottolineare sono la granulometria fine, che influisce positivamente sulla compattazione e sulla resistenza meccanica in essiccato dell’impasto, nonché la reologia e la sospensione negli smalti. ❱ Ball clay per plasticità e fusibilità Le argille plastiche (o ball clay) possono essere utilizzate in combinazione con il caolino quando il requisito della bianchezza è meno rigoroso: 86 < L* impasto < 88. Le soluzioni FMT e TSMA di Imerys hanno rappresentato un punto di riferimento importante nella produzione di gres porcellanato negli ultimi decenni in Europa e sui mercati extra-europei. Con il progressivo passaggio della produzione dai formati tradizionali alle grandi lastre, plasticità e pressabilità degli impasti diventano un requisito più che mai fondamentale. Le due argille citate presentano un altissimo livello di plasticità grazie alla loro ideale combinazione di caolinite, illite e smectite (montmorillonite) che fornisce eccezionali proprietà di bianchezza e plasticità, con una fusibilità standard. Per ottenere tali prestazioni, dal 5 al 10% di ball clay nella composizione dell’impasto è sufficiente per controllare la viscosità della barbottina. Tipicamente, l'argilla TSMA viene utilizzata per aumentare il MoR in essiccato di argille meno plastiche negli impasti bianchi standard di piastrelle in gres porcellanato; la FMT è invece preferita per aumentare il MoR di impasti bianchi per piastrelle o lastre in gres porcellanato in associazione con i caolini (Tab. 3).