PVC U transparent
Productcharacteristics
Normalimpactstrength
Hightransparency
verygoodprintable
Productapplications
Cleanroomandsemiconducterindustry
Mechanicalengineering
Advertisingtechnology
Materialdataiscollectedingoodfaithfromoursuppliers,alternativelyfromrawmaterialmanufacturers,andmaydifferdependingonthetest methodused.Toensuretherespectivevalue.NordicPlasticsGroupdisclaimsallresponsibilityinconnectionwiththeuseofthedata
Nordic Polytech Group, Omvägen 17, SE-231 61 Trelleborg, Sweden. Tel +46 (0)10-707 80 00 www.npgroup.se
General properties Test method UnitValue Density DIN EN ISO 1183-1 g/cm³1,40 Waterabsorption DIN EN ISO 62 %0,20 Flammability(thickness from 2mm)UL 94 V0 Flammability(thickness1mm … 5mm)NF P 92-501 M1 Flammability(thickness1mm … 5mm)DIN 4102 B1 Mechanical properties Test method UnitValue Yieldstress DIN EN ISO 527 MPa70 Elongation at break DIN EN ISO 527 %10 Tensilemodulus of elasticity DIN EN ISO 527 MPa3200 Notchedimpact strength DIN EN ISO 179 kJ/ m2 2 Shorehardness DIN EN ISO 868 scaleD83 Ball Hardness ISO 2039 MPa140 Bending Strenght DIN EN ISO 178 MPa 80 Thermal properties Test method UnitValue Vicat softeningtemperature DIN 53752 °C67 Service temperature Average °C-10…+50 Heat deflection temperature Average °C59 Coefficent of linearthermal expansionDIN EN ISO 306, Vicat Bmm/m K-0,075 Electrical properties Test method UnitValue Dielectricconstant IEC 60250 -3,2 Dielectricdissipation factor(106Hz) IEC 60250 -0,02 Volume resistivity DIN EN 62631-3-1 Ω * cm >1015 Surface resistivity DIN EN 62631-3-2 Ω >1013 Dielectricstrenght IEC 60243 kV/mm12 Comparativetracking index IEC 60112 CTI450
Version:2022