PVC U transparent Product characteristics Normal impact strength High transparency very good printable Product applications Clean room and semi conducter industry Mechanical engineering Advertising technology
General properties Density Water absorption
Test method DIN EN ISO 1183-1 DIN EN ISO 62
Unit g/cm³ %
Flammability (thickness from 2mm)
UL 94
V0
Flammability (thickness 1mm … 5mm)
NF P 92-501
M1
Flammability (thickness 1mm … 5mm) Mechanical properties Yield stress Elongation at break Tensile modulus of elasticity Notched impact strength Shore hardness Ball Hardness Bending Strenght Thermal properties Vicat softening temperature Service temperature Heat deflection temperature Coefficent of linear thermal expansion Electrical properties Dielectric constant Dielectric dissipation factor (106Hz) Volume resistivity Surface resistivity Dielectric strenght Comparative tracking index
DIN 4102 Test method DIN EN ISO 527 DIN EN ISO 527 DIN EN ISO 527 DIN EN ISO 179 DIN EN ISO 868 ISO 2039 DIN EN ISO 178 Test method DIN 53752 Average Average DIN EN ISO 306, Vicat B Test method IEC 60250 IEC 60250 DIN EN 62631-3-1 DIN EN 62631-3-2 IEC 60243 IEC 60112
B1 Unit MPa % MPa kJ / m2 scale D MPa MPa Unit °C °C °C mm/m K Unit Ω * cm Ω kV/mm CTI
Value 1,40 0,20
Value 70 10 3200 2 83 140
80 Value 67 -10…+50 59 -0,075 Value 3,2 0,02 >1015 >1013 12 450