PE 1000 Reg MC black Physical properties Molecular-weight Density Notched impact strength Abrasion-Index (Sand-Slurry) Tensile strength at yield (1 B - 50mm/Min.) Elongation (Break / 1 B - 50mm/Min.) Tensile-E-modulus (1B - 1mm/Min.) Static Friction Dynamic Friction Shore-D-Hardness, 3 sec. value 6 mm plate Ball indentation hardness Water absorption Thermal properties Melting Point (DSC) Thermal Conductivity Max. operation temperature Coefficient of thermal expansion (23 - 80°C) Electrical properties Volume resistivity Surface resistivity ATEX-Directive - TOV approved! ESD-D Burning properties Fire resistance (Self-classification) Fire resistance (Self-classification) Physiological properties
Test method k.a.
Unit
Value
2 Mio. g/mol.
2 Mio. g/mol.
DINENISO 1183-1 , ASTM D792 > 0.940 g/cm•> 58.682 lb/ft'
DINENISO 21304-2 DINENISO 15527 (05/2013)
> 30 kJ/m2 >14,265 ft-lb/in2 130-250 130-250 DINENISO 527-2, ASTM D 638 >20 N/mm2 >2900 psi DINENISO 527-2, ASTM D 638 >150 % >150 % 2 >700 N/mm 101500 psi DINENISO 527-2, ASTM D 638 ASTM D 1894 0.16-0,22 0.16-0,22 ASTM D 1894 0.10-0,17 0.10-0,17 DINENISO 868 64-68 D 64-68 D 2 38 N/mm DINENISO 2039 5510 psi DINENISO 62 < 0.01 % < 0.01 % Test method DINENISO 11357-1 Wire method Literature ISO 11359 Test method DINEN 62631-3-1 DINEN 62631-3-2 ATEX-Directive Test method DIN 4102 UL 94 Test method
Unit Value 133-137°C 271,4- 278,6 °F -0.41 W/m*K 2.84253 (BTU-in)/hr-ft2 80 ·c 176°F 0.00020mm/mm
0.000111 in/in °F
Unit
Value
1.0E+14 Ohm*cm 1.0E+14 Ohm*cm
1.0E+13 Ohm 1.0E+13 Ohm
Ohm Unit B2 Klasse HB Klasse Unit
Ohm Value B2 Class HB Class Value
Food compliant Material data is collected in good faith from our suppliers, alternatively from raw material manufacturers, and may differ depending on the test method used. To ensure the respective value. Nordic Plastics Group disclaims all responsibility in connection with the use of the data