ALL ZIRCONIA YOU NEED TT-ONE MULTILAYER
Your All-In-One
TT-ONE Multilayer
Multi-Functional Zirconia Solution
Suitable for all indications
Zirlux Complete exhibits 1000MPa that allows for a full accompaniment of indications ranging from single unit restorations to multiple units for rehabilitation cases. A consistent blend of shading elements combined with a cold isostatic pressing manufacturing process creates a highly esthetic ceramic. The consistency of the isostatic press provides an even distribution of strength and esthetics for consistent shade and strength with better clinical and patient acceptance. •
High strength, high translucency multi-layered zirconia with low opacity and more resistance fracture •
1000MPa
•
<47% Translucency
•
Reduce inventory costs with suitability for a wide range of indications
•
Spend less time post-processing with naturallooking esthetics and smooth transitional blend of shading characteristics
Physical Characteristics
Physical Characteristics (10.5 ± 1.0) x10 -6K-1 CTE after sintering (25-500°C) 3-point flexural strength after sintering
Z
( 10.5±1.0) x10 -6K -1
Y
<5%
<100μg/cm2
A
≥6.0g/cm3
CTE(25-500℃）
Accelerated aging surface monoclinic phase content Chemical solubility after sintering
Accelerated aging surface Cytotoxicity test monoclinic phase content
Radioactivity after sintering
Radioactivity
600MPa <5%
Density after sintering
Chemical solubility Sintering Temperature after sintering
C
≥6.0 g/cm3
Density before sintering
0 level <0.1Bq/g
2 <100μg/cm 1430~1470°C
F
<0.1Bq/g
E
(1450°C recommended) 1430-1550℃ recommend 1480℃
Sintering temperature
O
All 16 VITA® shades Now Available!*
A1
A2
A3
A3.5
A4
B1
B2
B3
B4
C1
C2
C3
C4
D2
D3
D4
BL1
BL2
Indications: • Full Contour Crowns • Full Contour Bridges • Veneers • Inlays/Onlays • Copings and Frameworks