QUOTE No.: NC8635
Certificate of Test
REPORT No.: FNC12946
COMBUSTIBILITY TEST FOR MATERIALS IN ACCORDANCE WITH AS 1530.1-1994
TRADENAME: Haymes Rendertex Renderbase Q Range Product – PM (polymer modified) Medium Grey
SPONSOR: Henry Haymes Proprietary Limited trading as Haymes Paints 1 Waringa Drive
BALLARAT VIC 3355
AUSTRALIA
DESCRIPTION OF
TEST SAMPLE: The sponsor described the tested specimen as a medium grade polymer-modified cement based plaster comprised of graded sand, crystalline silica, Portland cement, calcium hydroxide and non-hazardous ingredients
Nominal thickness: 50 mm
Nominal density: 1492.22 kg/m³ (measured)
Colour: grey
The test result only relates to the specimen tested and described in this report. CSIRO was not involved in the selection of the materials.
TEST PROCEDURE: Five (5) samples were tested in accordance with Australian Standard 1530 Methods for fire tests on building materials, components and structures, Part 1- 1994: Combustibility Test for Materials.
An alternative suitable insulating material was used to fill the annular space between the furnace tubes, as specified in Clause 4.2 of ISO 1182:2010.
RESULTS: The following calculated results were obtained, refer also to Summary of measurements:
DESIGNATION: The material is NOT deemed combustible according to the test criteria specified in Clause 3.4 of AS 1530.1-1994.
These test results relate only to the behaviour of the test specimens of the material under the particular conditions of the test and they are not intended to be the sole criterion for assessing the potential fire hazard of the material in use.
DATE OF TEST: 18 July 2022
Issued on the 30th day of August 2022 without alterations or additions.
Faustin Molina
Testing
Officer
Stephen Smith
Team
Leader,Reaction to Fire & Façade Fire Laboratory End of Report
Copyright CSIRO 2022 ©. Copying or alteration of this report without written authorisation from CSIRO is forbidden NATA Accredited Laboratory Number: 165
Corporate Site No 3625
Accredited for compliance with ISO/IEC 17025 - Testing
Page 1 of 2
Arithmetic mean = ���������������� �� Mean furnace thermocouple temperature rise (oC) 0.13 Mean specimen centre thermocouple temperature rise (oC) 0.04 Mean specimen surface thermocouple temperature rise (oC) 0.34 Mean duration of sustained flaming (s) 0 Mean mass loss (%) 6.77
End of Test Certificate
Page 2 of 2
OF MEASUREMENTS AND OBSERVATIONS OF SAMPLES UNDER TEST C12946 Parameters Symbol or expression Unit symbol Sample Number 1 2 3 4 5 Initial specimen mass msi g 108.63 108.27 110.38 111.78 109.61 Final specimen mass msf g 101.36 101.38 102.90 104.02 101.83 Mass loss �� = Msi ������ ������ x 100 % 6.69 6.36 6.78 6.94 7.10 Total duration of sustained flaming Cumulative total of duration of flaming* s 0 0 0 0 0 Initial furnace thermocouple temperature Tfi oC 750 752 750 745 752 Maximum furnace thermocouple temperature Tfm oC 770 758 764 773 768 Final furnace thermocouple temperature Tff oC 770 758 764 773 768 Furnace thermocouple temperature rise ���� =������ ������ oC 0 0 0 0 0 Maximum specimen centre thermocouple temperature Tcm oC 752 741 745 749 750 Final specimen centre thermocouple temperature Tcf oC 752 741 745 749 750 Specimen centre thermocouple temperature rise ���� =������ ������ oC 0 0 0 0 0 Maximum specimen surface thermocouple temperature Tcm oC 774 760 767 777 778 Final specimen surface thermocouple temperature Tsf oC 774 760 767 776 777 Specimen surface thermocouple temperature rise ���� =������ ������ oC 0 0 0 1 1 Test duration - min 55 45 55 60 65 Any individual duration flaming less than 5 seconds was discarded
SUMMARY