FLUORINE-FREE FABRICS Taking Steps Towards a Sustainable Future
2
EMBRACING FLUORINE-FREE TEXTILE FINISHES We designed fabrics to provide water and stain repellency (water- and dustborne) without relying on PFAS-based chemicals. As concerns over environmental sustainability continue to grow, it has become increasingly important for various industries to adopt eco-friendly practices. Due to PFAS’s persistence in the environment and potential health risks, there is a need for alternative solutions. In the domain of textile manufacturing, a significant shift towards fluorine-free finishes is manifesting itself.
ENVIRONMENTAL FRIENDLY
IMPROVED SUSTAINABILITY
Since PFAS substances are non-biodegradable, they remain in the environment long after their initial use. Choosing fluorine-free fabrics helps reduce the release of potentially harmful per- and polyfluoroalkyl substances (PFAS) into the environment, contributing to cleaner waterways and ecosystems.
Fluorine-free fabrics can be recycled at the end of their life, contributing to a closed-loop textile system. Fluorine-free fabrics require less energy during production compared to fabrics treated with fluorocarbonbased finishes.
3
UNDERSTANDING PFAS CHEMICALS AND THEIR IMPACT Perfluorinated compounds (PFAS) are a group of synthetic chemicals that have been widely used in the textile industry, providing fabrics with exceptional water and oil repellency, stain resistance and durability. Their applications range from workwear and medical apparel to outdoor textiles and upholstery. However, PFAS have been linked to persistent bioaccumulation, potential adverse health effects and environmental contamination.
VERSATILE PERFORMANCE
Fluorine-free fabrics provide water repellency and stain resistance equivalent to traditional fluorocarbon-based finishes, ensuring high-performance characteristics for various applications.
CHANGING LEGISLATION
Recognizing the risks of PFAS, commercial bodies and environmental organizations have imposed restrictions and bans on fluorinebased finishes. Also on the EU regulatory level, restrictions are being studied for future legislation.
4
OUR FLUORINE-FREE PRODUCTS Our team strives to develop solutions and alternatives, ensuring the best possible protection for professionals exposed to a variety of risks during their activities. This leads to a continuous expansion of our assortment: explore a selection of our fluorine-free finished fabrics, showing our commitment to innovation and sustainability. We are proud to present our latest breakthrough in textile technology that prioritizes both performance and eco-consciousness.
HEAVY DUTY FOREMAN REPREVE® FF COMPOSITION 34% CO / 34% PES / 32% PES REPREVE® WEIGHT 240 g/m² Ret < 5 m².Pa/W
FOREMAN STRETCH REPREVE® FF PBP COMPOSITION 33% PES RECYCLED / 30% PES REPREVE® / 16% CO PURFI® / 16% CO / 5% XLA® WEIGHT 280 g/m² Ret < 5 m².Pa/W
5 FOREMAN REPREVE® FF COMPOSITION 34% CO / 34% PES / 32% PES REPREVE® WEIGHT 240 g/m² Ret < 5 m².Pa/W
BIO FOREMAN AIR REPREVE® FF COMPOSITION 34% TENCEL® / 34% PES / 32% PES REPREVE® WEIGHT 260 g/m² Ret < 5 m².Pa/W
IRON FF COMPOSITION 100% PA 6.6 CORDURA® WEIGHT 260 g/m² Ret < 15 m².Pa/W
IRON RECYCLED FF COMPOSITION 100% PA 6.6 RE/COR® WEIGHT 260 g/m² Ret < 15 m².Pa/W
6
SOFTBRICK REPREVE® FF COMPOSITION 100% PES REPREVE® + FLEECE REPREVE® WEIGHT 270 g/m² Ret < 15 m².Pa/W
CORDUVIS FF COMPOSITION 100% PES CORDURA® WEIGHT 290 g/m² Ret < 5 m².Pa/W
COLDSTORAGE RECYCLED FF COMPOSITION 100% PA 6.6 RE/COR® WEIGHT 195 g/m² Ret < 15 m².Pa/W
CONDOR REPREVE® FF COMPOSITION 100 % PES REPREVE® WEIGHT 75 g/m² Ret < 5 m².Pa/W
WATERPROOF BREATHABLE POLEBRICK PES REPREVE® FF COMPOSITION 100% PES REPREVE® + PES MEMBRANE + FLEECE REPREVE® WEIGHT 325 g/m² Ret < 20 m².Pa/W
NORTHRAIN FF COMPOSITION 100% PES REPREVE® + PU COATING WEIGHT 155 g/m² Ret -
OMNIBRICK PES REPREVE® FF COMPOSITION 100% PES REPREVE® + PES MEMBRANE WEIGHT 150 g/m² Ret < 15 m².pA/W
NOTIO REPREVE® FF COMPOSITION 100% PES REPREVE® + PU COATED WEIGHT 170 g/m² Ret < 20 m².Pa/W
7
8
SNOWWIRE REPREVE® FF COMPOSITION 100% PES REPREVE® + PU COATED WEIGHT 200 g/m² Ret < 15 m².Pa/W
SHELTER FF COMPOSITION 100% PA6 + PU WEIGHT IN LABO Ret < 20 m².Pa/W
CHOOSING FLUORINE-FREE FABRICS HELPS REDUCE THE RELEASE OF HARMFUL SUBSTANCES INTO THE ENVIRONMENT.
FLAME RETARDANT PROTECTOR LIGHT FF COMPOSITION 55% MA / 44% CO / 1% AS WEIGHT 155 g/m² Ret < 5 m².Pa/W
OMNIPROTECTOR LIGHT PU FF COMPOSITION 55% MA / 44% CO / 1% AS + PU LAMINATED WEIGHT 260 g/m² Ret < 15 m².Pa/W
FLAMACRYL FLAMESTOP AS FF COMPOSITION 50% PES / 27% MAC / 22% CO / 1% AS WEIGHT 370 g/m² Ret < 5 m².Pa/W
PROTECTOR DOT NEW FF COMPOSITION 55% MA / 44% CO / 1% AS + PU COATED WEIGHT 365 g/m² Ret < 15 m².Pa/W
9
10
LIGHTWEIGHTS PIUMI FF COMPOSITION 100 % PA WEIGHT 42 g/m²
NAVIGATOR FF COMPOSITION 100% PA 6.6 WEIGHT 58 g/m²
MINIRIP FF COMPOSITION 100% PA 6 WEIGHT 75 g/m² Ret < 15 m².Pa/W
WALKER REPREVE® FF COMPOSITION 100% PES REPREVE® WEIGHT 78 g/m²
11
CONQUERING THE CHALLENGES Nonetheless, it is important to note that while fluorine-free finishes offer a more sustainable choice for workwear, they may have slightly different performance characteristics compared to traditional PFAS-based finishes. Therefore, it’s crucial to consider the specific requirements and intended use of the workwear when selecting the appropriate fluorine-free finish, ensuring it meets the desired level of water resistance, stain resistance and chemical repellency while also complying with necessary safety standards.
EXPLAINED
FF Fluorine-free PBP Powered by PURFI®