PC Hardcoat Clear General properties Bulk density °C Water absorption 24 h, 23 Mechanical properties Tensile strength
Test method Unit ISO 1183 g/cm³ ISO62 Test method Unit ISO 527 MPa Elongation at tear ISO 527 % Modulus of elasticity ISO 527 MPa Impact resistance ISO 179 Abrasion (Taber-process; 500 rotations;CS-1 OF; 500 g) ISO 9352 Thickness of layer Adhesive properties 0,5/1 ,0/2,0 h boiling period at 95°C ISO 2409 Thermal properties Test method Unit Vicat diluting temperature VST/B 50 ISO 306 °C Constancy temperature HOT/A ISO 75 °C (1,8 N/mm2)* Temperature of permanent use DIN 53446 °C Linear coefficient of cubical Thermal expansion (a) 0 -50 °C DIN 53752 Heat conductibility DIN 52612 Specific heat(c) Optical properties Test method Unit Refractive index Transparency 380-780 nm D = 3 mm DIN 5036 Deviation angle DIN 52305 Refractive power DIN 52305 Ω Electrical properties Test method Unit Specific volume resistivity DIN VDE 0303 Dielectric strength DIN EN 60243 Special properties Test method Unit Behaviour in fire DIN 4102, Fire classification B 2
Value 1,2 g/cm3 < 8 mg/kg Value 60 110 2200 unbroken 8 % Haze 4-8µm GT 0/0/0 Value 150 135 115 65 X 10·6 K·1 0,21 W/mK 1,3 J/gK Value 1 ,4425 86% 5 Bg' 0, l dpt Value l015Ωcm 30 kV/mm Value
Material data is collected in good faith from our suppliers, alternatively from raw material manufacturers, and may differ depending on the test method used. To ensure the respective value. Nordic Plastics Group disclaims all responsibility in connection with the use of the data
Nordic Polytech Group, Omvägen 17, SE-231 61 Trelleborg, Sweden. Tel +46 (0)10-707 80 00 www.npgroup.se Version: 2022