CK Conveyors IMPACT BARS CK IMPACT BARS ARE MADE FROM UNIQUE ABRASION AND IMPACT RESISTANT 60 SHORE NATURAL RUBBER WITH A 10MM POLYETHYLENE TOP. THE RUBBER COMPOUND PROVIDES EXCELLENT CUSHIONING AND IMPACT ABSORPTION. THE 6MM OR 12MM THICK, LOW FRICTION UHMWPE TOP LAYER, PROVIDES A PROTECTIVE SURFACE PREVENTING WEAR AND DAMAGE. EASILY INSTALLED USING THE M16 BOLTS SUPPLIED, THE METAL CHANNEL RUNNING THE LENGTH OF EACH IMPACT BAR ENABLES EASY FIXING AND REMOVAL. LONG BOLTS AVAILABLE ON REQUEST.

These complete impact cradles not only minimise maintenance by out lasting conventional rollers but they hold the belt in position therefore significantly reducing transfer point spillage.

STANDARD SIZES Width

Thickness

Length

Capping Thickness

100mm

55mm

1240mm

6mm

100mm

75mm

1240mm

6mm

100mm

55mm

1240mm

12mm

100mm

75mm

1240mm

12mm

• Bars available ex stock • Fast delivery to site • Low price guarantee

ADVANTAGES • Spillage significantly reduced therefore less downtime in cleaning out from under conveyors.

• Can supply impact cradles complete or a variety of belt widths.

• Unique abrasion and impact resistant qualities of natural rubber • Cost effective, easy to fit and radiused top edges prevent damage to belts. • The belt is supported on a continuous flat surface which not only guides it but protects it from gouging by sharp material. • Equal stress distribution reduces wear and tear on the belt.

1 BIGGER ROAD, CLELAND, MOTHERWELL, LANARKSHIRE, ML1 5PB

Tel: 01698 862123 Fax: 01698 862383

Email: sales@ckconveyors.com

CK CONVEYORS www.ckconveyors.com


CK CONVEYORS Data Sheet Advanced Conveyor Components

Impact Bars – Green and White Capping White Capping

Green Capping

Typical Value

Typical Value

Grade

1000

Reclaimed 1000

Colour

White

Green

0.94

0.96

Tensile Break (MPa)

22

22

Breaking Strength (MPa)

44

43

Elongation at Break (%)

>350

>350

61

61

-60 to 120C

-60 to 120C

Volume Resistivity (Ohm cm)

>1015

>1015

Surface Resistivity (Ohm)

>1013

>1013

Torsional Stiffness (MPa)

250

300

Melting Point (C)

137

139

Thermal coefficient of linear expansion 23-80C (C-1 1/K)

1.7 – 2.5 x 10-4/K

1.7 – 2.5 x 10-4/K

Thermal Conductivity at 23C (W/C x m)

0.42

0.42

80

80

80 - 100

110 - 120

UHMWPE Property

Specific Gravity

Hardness (Type D) Service temperature (C)

Dimensional stability under heat (C) Abrasion (Sand-Slurry test) %

IBC Rubber cushion compound Tensile Strength (MPa)

15.4

Elongation (%)

600

Modulus 300% (MPa)

4.0

Specific Gravity

1.13

Hardness (IRHD)

61

Tear Strength (N/mm)

56

Additional Requirements: None