Abstract:- The results of an investigation which was undertaken to reveal the differences in the mechanical properties and microstructural characteristics of two types of Ni-hard cast irons are presented in this study. The cast irons were obtained in a laboratory conditions and their compositions are in accordance with European standard EN 12513. One type of cast iron is EN GJN-HV520 (Ni-hard 2) containing 2.10% Cr and the second type EN GJN-HV600 (Ni-hard 4) with 9.04% Cr. The cast irons were evaluated in both as-cast and heat treated conditions. To improve mechanical properties specifically wear resistance, the samples of both types Ni-hard cast irons were subjected to different heat treatment processes. Annealing of Ni-hard 2 samples at 480°C during 4 hours caused increasing of hardness for about 13.5% due to additional precipitation of secondary carbides. On the other hand the heat treatment process consisting of annealing at 790°C during 4-8 hours of Ni-hard 4 samples, compared to