Magnet Wire Hermincel 200°C Typical properties (18 AWG HD Type)
External Diameter 4 point measured separated 45°C
1,110 mm Maximum
Gradual elongation at rupture
Adherence & Flexibility
20% elongation and wrapped around a mandrel 3 times of nominal bare diameter.
No cracks visible in the film coating
Unidirectional (by NEMA)
1150g Mínimum average
20% elongation and wrapped around a mandrel 3 times of nominal bare diameter and heated 30 min. at 220°C.
SNo cracks visible in the film coating
2000 g load (by NEMA)
10 minutes preheated at 150°C and inmersed at 60°C in Butyl Cello solve and Xylene
No soften sufficiently to expose the bare conductor
Dielectric Strength Continuity Dielectric Strength at Nominal Temperature
5700 V NEMA Method Faults in 30.48 m
5 Maximum 4275 V
NEMA Method Note: Results obtained at CENTELSA’s Laboratories according to NEMA MW 1000 and NTC 361.
9000 V 0 7500 V