Cu-XLP/PHC Extra low phosphorous copper (P content 10‌50 (60) ppm), earlier known as SE-Cu58.

Properties: Good electrical and thermal conductivity Resists hydrogen embrittlement Excellent corrosion resistance Excellent formability Good weld ability High scrap value Composition: Cu min 99,95 % P 10‌50 ppm Electrical conductivity: min 100 % IACS According to EN: H040 min 100 % IACS, H065-90 min 98,3 % IACS, H110 min 96,6 % IACS

Typical applications: Power distribution systems, telecommunication cables, electrical and electronic applications

1 (3)


Alloy name

Cu-XLP

European standard number UNS code Manufacturing location

C10300 Pori

Chemical properties

P 0.001-0.005 %

Physical Properties

Density

g/cm3 lb/in3 Electrical Conductivity**** (Nominal value in black) %IACS Thermal Conductivity W/(m °K) Btu/ft h °F Modulus of Elasticity GPa X1000 ksi Coef. of Thermal Exp. at 20 ºC (68 ºF) 10-6/°C 10-6/°F

8.9 0.323 min min

100 100

min min

386 223 117 17 17.6 9.8

Tempers Mechanical Properties EN H040 / R200

Tensile Strength Rm N/mm2 Yield Strength (0.2 %)N/mm2 Elongation % A50 / A Hardness (HV) Thickness mm (Pori)

max min

EN H040 / R220

Tensile Strength Rm N/mm2 Yield Strength (0.2 %)N/mm2 Elongation % A50 / A Hardness (HV) Thickness mm (Pori)

max min

EN H065 / R240

Tensile Strength Rm N/mm2 Yield Strength (0.2 %)N/mm2 Elongation % A50 / A Hardness (HV) Thickness mm (Pori)

min min

EN H090 / R290

Tensile Strength Rm N/mm2 Yield Strength (0.2 %)N/mm2 Elongation % A50 / A Hardness (HV) Thickness mm (Pori)

EN H110 / R360

Tensile Strength Rm N/mm2 Yield Strength (0.2 %)N/mm2 Elongation % A50 / A Hardness (HV) Thickness mm (Pori)

min min

min min min min

200 - 250 100 - / 42 40 - 65 0.2 - 20 220 - 260 140 33 / 42 40 - 65 0.2 - 20 240 - 300 180 8 / 15 65 - 95 0.2 - 6, 12 - 25 290 - 360 250 4/6 90 - 110 0.2 - 25 360 320 2/ 110 0.2 - 20

2 (3)


Alloy name

Cu-PHC

European standard number UNS code Manufacturing location

C10300 Pori

Chemical properties

P 0.001-0.006 %

Physical Properties

Density

g/cm3 lb/in3 Electrical Conductivity**** (Nominal value in black) %IACS Thermal Conductivity W/(m °K) Btu/ft h °F Modulus of Elasticity GPa X1000 ksi Coef. of Thermal Exp. at 20 ºC (68 ºF) 10-6/°C 10-6/°F

8.9 0.323 min min

100 100

min min

386 223 117 17 17.6 9.8

Tempers Mechanical Properties EN H040 / R200

Tensile Strength Rm N/mm2 Yield Strength (0.2 %)N/mm2 Elongation % A50 / A Hardness (HV) Thickness mm (Pori)

max min

EN H040 / R220

Tensile Strength Rm N/mm2 Yield Strength (0.2 %)N/mm2 Elongation % A50 / A Hardness (HV) Thickness mm (Pori)

max min

EN H065 / R240

Tensile Strength Rm N/mm2 Yield Strength (0.2 %)N/mm2 Elongation % A50 / A Hardness (HV) Thickness mm (Pori)

min min

EN H090 / R290

Tensile Strength Rm N/mm2 Yield Strength (0.2 %)N/mm2 Elongation % A50 / A Hardness (HV) Thickness mm (Pori)

EN H110 / R360

Tensile Strength Rm N/mm2 Yield Strength (0.2 %)N/mm2 Elongation % A50 / A Hardness (HV) Thickness mm (Pori)

min min

min min min min

200 - 250 100 - / 42 40 - 65 0.2 - 20 220 - 260 140 33 / 42 40 - 65 0.2 - 20 240 - 300 180 8 / 15 65 - 95 0.2 - 6, 12 - 25 290 - 360 250 4/6 90 - 110 0.2 - 25 360 320 2/ 110 0.2 - 20

3 (3)


CuXLP PHC Aurubis